Early stage phase transformations and coarsening of an Al-Li-Zr alloy
Al-Li-Zr alaşımında faz dönüşümleri ilk aşamaları ve çökelti büyümesi
- Tez No: 15528
- Danışmanlar: DOÇ. DR. ŞAKİR BOR
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Al-Li alaşımları. uyumlu düzeni eşme, çök el t i büyümesi, kompozit çökeltiler, transmisyon elektron mikroskobunda ısıtma, Alüminyum, Elektron mikroskobu, Lityum, Çökelti büyümesi, Al-Li alloys, congruent ordering, Al Li precipitate coarsening, composite precipitates, hot stage transmission electron microscopy, Aluminum, Electron microscope, Composite precipitate, Lithium, Sediment growth
- Yıl: 1991
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Belirtilmemiş.
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Al- 3. 52%Li- O. ISJSZr - l.aa%Cu -0.68%Mg alaşımında faz dönüşümlerinin ilk aşamaları çeşitli transmisyon elektronmi krosköp yöntemleri yine incelendi. Üstkafes karanlık alan görüntülerinin incelenmesiyle, dönüşümün tüm yapının, bileşim değişimi olmaksızın düzenli hale gelmesi ( uyumlu düzenleşme) ve bunu takiben ö'C Al LİD fazının spinodal olarak ayrışması olarak belirlenmiştir. Bu çalışmada hızlı soğutma sırasında uyumlu düzenleşmenin tamamlandığı ve spinodal ayrışmanın başladığı gözlenmiştir. Karanlık alan görüntülerindeki yaşlandırma ile gözlenen kontrast değişimleri, spinodal ayrışmanın devam ettiğini ve 6' fazının denge halindeki bileşimine ulaşırken ana yapının Li kaybı dolayısıyla düzensiz hale geldiğini göstermiştir. 6' çökelti büyümesi, 443 K, 473K ve SOS K da 83.8 ks süresine kadarvaranyaşlandırmaişlemleriyle incelenmiştir. Büyüme kinetiğinin tkuralına uyduğu vgözlenmiştir. Ancak yüksek yaşlandırma sıcaklıklarında yüzey kontrollü büyümenin, t. varlığına işaret eden olgular da bulunmuştur. Parça boyutu dağılımlarının Lishfitz-SLyozov-Wagner CLSWD ve bunun modi fi ye edilmişi CMLSWD büyüme teorilerine göre daha geniş ve simetrik olduğu ortaya çıkmıştır. /3'CA1 ZrD çökeltileri üzerine heterojen Ayrıca bazı 6' parçacıklarının yapı içinde bulunan olarak çekirdeklenmesiyle başlayan ve karanlık alan görüntülerinde çok karmaşık ve değişken kontrast gösteren kompozit çökeltiler de gözlenmiştir. îleri safhalarda bu 6' parçacıklarının büyüyerek (3' çökeltisini tamamen kavradığı ve karakteristik çift fazlı çökelti görünümünü aldığı saptanmıştır. Al Li 3
Özet (Çeviri)
The early stages of precipitation in an Al- 2.52%Li- 0.15%Zr- 1.22%Cu- 0.68%Mg alloy have been studied by conventional and hot stage transmission electron microscopy techniques. The superlattice dark field observations confirm that the transformation path is congruent nonstoichiometric ordering of the matrix followed by spinodal decomposition of 6' (Al Li) phase. In the present alloy the congruent ordering is accomplished and subsequent spinodal decomposition is initiated during quenching. Follow-up of contrast variations during aging suggests that, with continuing spinodal decomposition the <5' approaches to its stoichiometry while the matrix disorders due to associated Li depletion. Coarsening behavior of the <5' precipitates has been studied by aging treatments at 443 K, 473 K and 503 K for iiiperiods up to 82.8 ks. It was found that the coarsening 1/3 kinetic obeys t power law, but indications of surface 1/2 controlled type coarsening, t, were also seen at higher aging temperatures. Particle size distributions were observed to be broader and more symmetrical than those of the Lishfitz-Slyozov-Wagner (LSW) and the modified type (MLSW) coarsening theories. In addition, some 6' was observed to nucleate heterogeneous ly on existing ft' (Al9Zr) particles resulting in composite precipitates with rather complex and variable contrast. The 6' precipitates initially formed by epitaxial nucleation subsequently grows to envelop the ft' particles giving the characteristic dough-nut shape.
Benzer Tezler
- GGG 50 ve GGG 80 sınıfı küresel grafitli dökme demirlerin abrasiv aşınma davranışına ostemperleme işleminin etkisi
The influence of a austempering process on the abrasive wear properties of GGG 50 and GGG 80 grade ductile irons
MEHMET UMUT KÖKDEN
Yüksek Lisans
Türkçe
1998
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
PROF. DR. HÜSEYİN ÇİMENOĞLU
- Alt-uzay dönüşüm yöntemi ile Fır süzgeç tasarımı
Finite-duration impulse response filter design using subspace transformations
MEHMET DEVRİM AZAK
Yüksek Lisans
Türkçe
1997
Elektrik ve Elektronik Mühendisliğiİstanbul Teknik ÜniversitesiElektronik ve Haberleşme Mühendisliği Ana Bilim Dalı
PROF. DR. ALİ NUR GÖNÜLEREN
- Li2O - ZnO - Al2O3 camlarının kontrollü kristalizasyonu ve cam seramiklerin karakterizasyonu
The Controlled crystallization of Li2O - ZnO - Al2O3 - SiO2 glasses and the characterization of glass ceramics
ENGİN MAYTALMAN
Yüksek Lisans
Türkçe
1999
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
DOÇ. DR. ERDEM DEMİRKESEN
- Gölbaşı'nda (Ankara) metamorfik kayaçlar (Şistler) üzerinde oluşmuş toprakların kil mineralojileri ve genesisleri
Başlık çevirisi yok
NEDİM ÖZENÇ