Çok katyonlu oksinitrür cam sistemlerinde B-fazının (Ln2SiA1O5N, Ln=Y-Sm; Y-Ce) kararlılığı
The stability of B-phase (Ln2SiA1O5N, Ln=Y-Sm; Y-Ce) in multi cation doped oxynitride glass systems
- Tez No: 150584
- Danışmanlar: PROF. DR. HASAN MANDAL
- Tez Türü: Yüksek Lisans
- Konular: Seramik Mühendisliği, Ceramic Engineering
- Anahtar Kelimeler: B-Fazı (LmSiAlC^N), Çok Katyon, Oksinitrür Cam, B-Phase (Ln2SiA105N), Multi Cation, Oxynitride Glass
- Yıl: 2004
- Dil: Türkçe
- Üniversite: Dumlupınar Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Seramik Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
IV ÇOK KATYONLU OKSİNİTRÜR CAM SİSTEMLERİNDE B-FAZINTN (Ln2SiAIOsN, Ln= Y-Sm ; Y-Ce) KARARLILIĞI Hilmi Yurdakul Seramik Mühendisliği, Yüksek Lisans Tezi, 2004 Tez Danışmanı: Prof. Dr. Hasan MANDAL ÖZET Ln2SiA105N kompozisyonunda alüminyum içeren bir a-wollastonit olan B-fazı, itriyum oksit ve yüksek atom numarasına sahip nadir toprak element (rc^ 0.908 Â) oksitleri ile yoğunlaştırılmış p- ve a~P SiAlON seramiklerinde taneler arası camsı fazdan kolay bir şekilde devitrifiye olur. Sm+3 (0.964 Â) ve Ce+3 (1.036 Â) katyonları büyük katyon yarıçapına sahip olduklarından dolayı, bu katyonlar tek başlarına hegzogonal kristal yapısındaki B-fazını (Ln2SiA105N, Ln= Lu, Yb, Er, Y ve Dy) kararlı kılamazlar. Bu çalışmada, B-fazımn yapısını kararlı kılan Y1"3 (0.893 Â) katyonu ile Sm+3 (0.964 Â) ve Ce+3 (1.036 A) katyonlarının değişik molar oranlarda oluşturduğu çok katyonlu [Y+3 (0.893 Â) - Sm+3 (0.964 A) ; Y*3 (0.893 A) - Ce+3 (1.036 A)] oksinitrür cam sistemlerinde, Sm+3 (0.964 A) ve Ce+3 (1.036 A) katyonlarının B-fazmm yapışma girmesi amaçlanmıştır. Çok katyonlu oksinitrür cam s istemleri B-fazı ana cam kompozisyonu olarak bilinen atomca % M15.2Sİ14.6Aİ8.7054.6N6.9 kompozisyonu (M= %100Y, %75Y-%25Ce, %50Y-%50Ce, %25Y-%75Ce, %100Ce; %75Y-%25Sm, %50Y- %50Sm, %25Y-%75Sm ve %100Sm) esas alınarak hazırlanmıştır. Her bir sistem için elde edilen toz karışımları isopropil alkol kullanılarak agat havan içerisinde karıştırıldıktan sonra kurutulup tek eksenli preste şekillendirilmiştir. Şekillendirilen ürünler atmosfer kontrollü yüksek sıcaklık fırınında azot atmosferinde BN pota içerisinde 1700 °C de 0.1 MPa azot basıncında oksinitrür cam elde etmek için 1/2 saat süreyle ergitilmişlerdir. Elde edilen oksinitrür camlara daha sonra SiC ısıtıcı elemanh yatay tüp fırında B-fazını elde etmek amacıyla azot atmosferinde 1070 °C de 17 saat ısıl işlem uygulanmıştır. X-ışmı difraksiyon analizi (XRD) sonuçları ve hesaplanan latis parametrelerine göre, Sm+3 (0.964 A) katyonunun çok katyonlu K6 (%75Y-%25Sm) ve K7 (%50Y-%50Sm) kompozisyonlarında, Ce+3 (1.036 A) katyonunun ise çok katyonlu K2 (%75Y-%25Ce) kompozisyonunda B-fazınm (Ln2SiA105N, Ln= Y-Sm; Y-Ce) yapısını kararlı kıldığı görülmüştür.
Özet (Çeviri)
THE STABILITY OF B-PHASE (Ln2SiA10sN, Ln = Y-Sra ; Y-Ce) IN MULTI CATION DOPED OXYNITRTDE GLASS SYSTEMS Hilmi Yurdakul Ceramic Engineering, M.S. Thesis, 2004 Thesis Supervisor: Prof. Hasan MANDAL SUMMARY B-phase, which is an aluminium-containing oc-wollastonite of composition Ln2SiA105N, easily devitrifies from the intergranular glassy phase in P- and a-(3 SiAlON ceramics densified with yttrium oxide and high atomic number rare earths oxides (rc< 0.908 Â). Since Sm+3 (0.964 Â) and Ce+3 (1.036 Â) cations have high cation radius, these cations don't only stabilize B- phase (Ln2SiA105N, Ln= Lu, Yb, Er, Y and Dy) hexagonal crystal structure. In present research, The incorporating of Sm+3 (0.964 Â) and Ce+3 (1.036 Â) cations into B-phase crystal structure was aimed in multi cation doped oxynitride glass systems [Y+3 (0.893 Â) - Sm+3 (0.964 Â) ; Y*3 (0.893 Â) - Ce+3 (1.036 A)] to be combined in various molar ratios of Sm+3 (0.964 Â) and Ce+3 (1.036 Â) cations with Y*3 (0.893 Â) cation which stabilizes B-phase crystal structure. Multi cation doped oxynitride glass systems were prepared to based on (a/6) % M15.2Sii4.6Aİ8.7054.<;N6.9 composition (M= %100Y, %75Y-%25Ce, %50Y-%50Ce, %25Y-%75Ce, %100Ce; %75Y- %25Sm,'%50Y-%50Sm, %25Y-%75Sm and %100Sm) which was known as B-phase parent glass composition. Prepared powder mixtures for each system were mixed by using isopropyl alcohol in agate pestle and mortar then they were dried and pressed with an uniaxially press. Formed samples were melted in BN crucible at 1700 °C and 0.1 MPa nitrogene pressure in nitrogene atmosphere within atmosphere controlled high temperature furnace for 30 minute in order to get oxynitride glasses. Obtained oxynitride glasses were then heat treated in a horizontal furnace with SiC heating element in nitrogene atmosphere at 1070 °C for 17 hour in order to get B-phase. The results of X-ray diffraction (XRD) analysis and according to calculated lattice parameters; It was seen that Sm+3 (0.964 Â) cation in multi cation doped K6 (%75Y-%25Sm) and K7 (%50Y-%50Sm) compositions and Ce+3 (1.036 Â) cation in K2 (%75Y-%25Ce) composition would stabilized structure of B-phase (Ln2SiA105N, Ln= Y-Sm; Y-Ce).
Benzer Tezler
- Chemical synthesis of multi-cation oxide powders for solid oxide fuel cell (SOFC) components
Katı oksit yakıt pili (KOYP) elemanları için çok katyonlu oksit tozların kimyasal sentezi
ÇINAR ÖNCEL
- Alfa-SiAlON faz bölgesinin tespiti ve mikroyapısının karakterizasyonu
The Investigation of phase stability region and microstructural characterization of a alpha-SiAlONs
SEMRA KURAMA
Doktora
Türkçe
2003
Seramik MühendisliğiAnadolu ÜniversitesiSeramik Mühendisliği Ana Bilim Dalı
PROF. DR. HASAN MANDAL
- Potasyum bikromatın kristal büyümesine ortak iyon etkisi
Common ion effects on the crystal growth behaviour of potassium bichromate
M. BURCU KUŞKAY
Yüksek Lisans
Türkçe
2002
Kimya Mühendisliğiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. A. NUSRET BULUTCU
- 1,2-1,8-Antrakinon substitue makro halkalı eter sentezleri
The Synthesis of 1,2- and 1,8-antraquinone derivaties of crown ethers
ERBAY ERBAY
- High temperature chemistry of some borophosphates, phase relations and structural studies
Bazı yeni borofosfat bileşiklerinin yüksek sıcaklık kimyası, faz bağıntıları ve yapı çalışmaları
SEMİH SEYYİDOĞLU
Yüksek Lisans
İngilizce
2003
KimyaOrta Doğu Teknik ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. MERAL KIZILYALLI