Yba2Cu3--xRexOy(x=0, 0,3, 0,5, 0,7, ve 1,0 ve Re=Yb, Sm, Nd) süperiletkenlerinin yapısal ve fiziksel özelliklerinin incelenmesi
Investigation of structural and physical properties of Yba2Cu3--xRexOy(x=0, 0,3, 0,5, 0,7, and 1,0 ve Re=Yb, Sm, Nd) superconductors
- Tez No: 139239
- Danışmanlar: PROF.DR. EKREM YANMAZ
- Tez Türü: Doktora
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: Süperiletken, Katıhal Tepkime Yöntemi, FQMG Yöntemi, Nd Katkısı, Manyetik Kaldırma Kuvveti, Kritik Akım Yoğunluğu, Bean Modeli, Superconductor, Solid State Method, FQMG Method, Nd Adding, Magnetic Levitatin Force, Critical Current Density, Bean Model. VI
- Yıl: 2003
- Dil: Türkçe
- Üniversite: Karadeniz Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET Bu çalışmada YBa2Cu3.xRexOy (Re=Yb, Sm, Nd) olacak biçimde, katıhal tepkime (x=0, 0,3, 0,5) ve alevde eritme-hızlı soğutma-büyütme (FQMG) (x=0, 0,3 0,5 0,7, 1,0) yöntemleri kullanılarak numune üretimi yapıldı. Bu numunelerin bazı yapısal ve fiziksel özellikleri, x-ışını kırınım desenleri, SEM/optik mikro fotoğrafları, manyetik kaldırma kuvveti ölçümleri, direnç ölçümleri ve son olarak AC alınganlık ölçümleri bakımından incelendi. Buna göre katıhal tepkime yöntemi ile üretilen numunelerde katkının yapı içine girmediği, katkıyla birlikte numunelerin süperiletkenlik özelliklerinin bozulduğu tespit edildi. FQMG yöntemi ile üretilen numunelerde ise katkının yapı içine girdiği ve bu suretle x=0,3 Yb katkılı numune ile x=0,3 Nd katkılı numunelerin bazı süperiletkenlik özelliklerinde iyileşme meydana geldiği gözlendi. x=0,3 Yb katkılı numunenin sıvı azot sıcaklığında ölçülen manyetik kaldırma kuvvetinin maksimum değeri katkısız numuneden ~%240 daha büyük ölçüldü. x=0,3 Nd katkılı numunenin, AC alınganlık ölçüm verilerinden Bean modeli kullanılarak hesaplanan, kritik akım yoğunluğu katkısız numuneden %235 oranında büyük bulundu. Basit bir model geliştirilerek numunelerin, manyetik kaldırma kuvveti ölçüm verilerinden yararlanarak, alanın fonksiyonu olarak kritik akım yoğunlukları hesaplandı. Kaldırma kuvveti ile AC alınganlık ölçüm verilerinden teorik olarak hesaplanan kritik akım yoğunluğu değerleri aynı sıcaklık ve alan için birbirleriyle kıyaslandığında, AC alınganlık ölçümlerinden bulunanların daha büyük olduğu görüldü. Bu farklılığın çökelti fazlarından olduğu sonucuna varıldı.
Özet (Çeviri)
SUMMARY Investigategation of Structural and Physical Properties of YBa2Cu3-xRexOy (x=0, 0.3, 0.5, 0.7, 1.0 and Re=Yb, Sm, Nd) Superconductors In this work, sample production in the form of YBa2Cu3.xRexOy (Re=Yb, Sm, Nd) has been carried out by using solid state reaction (x=0, 0.3, 0.5) and Flame-Quench-Melt Growth (FQMG) (x=0, 0.3, 0.5, 0.7, 1.0) techniques. Some structural and physical properties of the samples prepared by two methods have been investigated using x-ray diffraction (XRD), SEM/optical micrographs, magnetic levitation force, resistivity and finaly AC susceptibility measurements. Therefore, it was found that the substitution of above elements did not enter into the unit cells of the samples prepared by solid state reaction method and the superconducting properties of all samples were destroyed with increasing the content of substitution in samples. For the samples prepared with FQMG method, the substitutions mentioned above were observed to enter into the unit cell of the samples, thus, it was observed that the substitution of x=0.3 Yb and x=0.3 Nd improved some superconducting properties of the samples. The maximum value of the magnetic levitation force, measured at liquid nitrogen temperature, on the x=0.3 Yb sample is found to be ~%240 greater than that of the pure sample. Critical current density of x=0.3 Nd calculated using the Bean model is found to be ~%235 greater than that of pure sample. Critical current densities as a function of the magnetic field are calculated by developed a simple method based on magnetic levitation force measurement data. Comparision of critical current densities obtained from levitation force and calculated theoretically from AC susceptibility measurement data, for the same temperature and field strength, showed that the values obtained from AC susceptibility measurements are greater. It was attributed to the amounts of precipitations in samples.
Benzer Tezler
- ZnO ilavesinin YBa2Cu3O7-x süperiletkenlerin yapısal, mekaniksel ve manyetik özellikleri üzerine etkisi
Effect of ZnO additions on the structural, mechanical and magnetic properties of YBa2Cu3O7-x bulk superconductors
UĞUR KÖLEMEN
Doktora
Türkçe
2002
Fizik ve Fizik MühendisliğiKaradeniz Teknik ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. SELAHATTİN ÇELEBİ
- Gümüş difüzyonunun YBa2Cu3O7 süperiletkeninin yapısal ve süperiletkenlik özellikleri üzerine etkisi ve süperiletkenlik durumuna göre x-ışını üretim tesir kesiti ve flüoresans verim değerlerinin değişimi
The effect of silver diffüsion on structural and superconductor behaviours of the YBa2Cu307 supercoductor and changing of the x-ray cross sections and flüorescence yields according to the superconductor condutions
OĞUZ DOĞAN
Yüksek Lisans
Türkçe
2000
Fizik ve Fizik MühendisliğiAtatürk ÜniversitesiFizik Ana Bilim Dalı
DOÇ. DR. MEHMET ERTUĞRUL
- Püskürtüm sistemi yapılması ve yüksek sıcaklık üstüniletken ince filmlerin hazırlanması
Construction of sputtering system and preparation of high temperature superconducting thin films
ERDAL KAYNAK
Doktora
Türkçe
2000
Fizik ve Fizik MühendisliğiHacettepe ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. FIRAT TEZER
- YBCO süperiletken bileşiğine yabancı atom katkısının etkileri
Effects of foreign atom doping into the YBa2Cu3O7 superconducting compound
HATİCE KOÇOĞLU
Yüksek Lisans
Türkçe
2003
Fizik ve Fizik MühendisliğiEge ÜniversitesiFizik Ana Bilim Dalı
YRD. DOÇ. DR. MUSTAFA TEPE
- YBa2 Cu3 O7-8 bileşiğinde Y yerine farklı iyonik yarıçapa sahip Nd katkılanmasının etkisi
Başlık çevirisi yok
TEKİN İZGİ
Yüksek Lisans
Türkçe
2001
Fizik ve Fizik Mühendisliğiİnönü ÜniversitesiFizik Ana Bilim Dalı
Y.DOÇ.DR. H. İBRAHİM ADIGÜZEL