SiC parçacık takviyeli 7075 alüminyum alaşım matrisli kompozit malzemlerin difüzyon kaynağı

Diffusion welding of SiC particle reinforced 7075 aluminium alloy matrix composites

  1. Tez No: 133450
  2. Yazar: MUSTAFA AYDIN
  3. Danışmanlar: PROF. DR. REMZİ GÜRLER, PROF. DR. MEHMET TÜRKER
  4. Tez Türü: Doktora
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: MetaI matrisli kompozit malzeme, difuzyon kaynağı, aratabaka, vortex yöntemi, SiC parçacık, Alüminyum alaşımları, Difüzyon kaynağı, Kompozit malzemeler, Metal matrisli kompozitler, Vorteks yöntemi, Metal matrix composites (MMC), diffusion welding, interlayer, vortex method, SiC particle, Aluminum alloys, Composite materials, Metal matrix composites
  7. Yıl: 2003
  8. Dil: Türkçe
  9. Üniversite: Gazi Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metal Eğitimi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

SiC PARÇACIK TAKVİYELİ 7075 ALÜMİNYUM ALAŞIM MATRİSLİ KOMPOZİT MALZEMELERİN DİFÜZYON KAYNAĞI (Doktora Tezi) Mustafa AYDIN GAZİ ÜNİVERSİTESİ FEN BİLİMLERİ ENSTİTÜSÜ Haziran 2003 ÖZET Bu çalışmada, metal matristi kompozit malzeme (MMK), ergimiş metal karıştırma (vortex) yöntemiyle üretilip, diffizyon kaynak yöntemiyle birleştirilmiştir. MMK malzeme, 7075 alüminyum alaşım içerisine ortalama 40 mikron boyutlarında SiC parçacıktan ağırlıkça %3 ilave edilerek üretilmiştir. Üretilen malzemeleri birleştirmek için difuzyon kaynak cihazı tasarlanıp, imal edilmiştir. Numuneler difuzyon fırını için uygun boyutlara getirilip, bakır ve gümüş aratabakalı ve aratabakasız olarak difuzyon kaynak yöntemiyle birleştirilmişlerdir. Kaynak işlemlerinden sonra, numuneler kaynak birleşme arayüzeyine dik olarak kesilip, birleşme arayüzeylerinde mikroyapı, SEM, EDS analizi çalışmaları yapılmıştır. Mekanik test olarak mikroserdik ölçümü ve kesme testi yapılmıştır. Kesme testleri, imalatı yapılan bir aparat ile ölçülmüştür. Matris malzemesi, kompozit malzeme ve kaynaklı numunelerden elde edilen kesme testi değerleri birbirleri ile karşılaştırılmıştır. Yapılan optik mikroskop çatışmalarında, kompozitin homojen bir karışıma sahip olduğu ve gözenek miktarının düşük olduğu görülmüştür. Mikrosertlik deney sonuçlarında, matris alaşım ile üretilen MMK malzeme arasında kaynaklı birleştirilmiş ve kaynakla birleştirilmeyen numuneler de çok az sertlik artışı görülmüştür. Aratabakalı kaynaklı birleştirmelerden bakır aratabakalıkaynakta, gümüş aratabakalı kaynağa göre daha yüksek sertlik artışı görülmüştür. EDS analizlerinde ise, gümüş aratabakalı kaynaklı birleştirmede daha uzak mesafelerde difuzyon görülmüştür. Kesme testi sonuçlarında, gümüş aratabakalı kaynaklı birleştirme, bakır aratabakalı kaynaklı birleştirmeden daha düşük değerler vermiştir. Fakat aratabakasız MMK malzemenin kaynaklı birleştirmesi en yüksek kesme mukavemeti değeri vermiştir. Bilim Kodu :6261901

Özet (Çeviri)

DIFFUSION WELDING OF SiC PARTICLE REINFORCED 7075 ALUMINIUM ALLOY MATRIX COMPOSITES (Phd.Thesis) Mustafa AYDIN GAZI UNIVERSITY INSTITU OF SCIENCE AND TECHNOLOGY June 2003 ABSTRACT In this study, metal matrix composite (MMC) materials, which was produced by vortex method, were bonded by diffusion welding. MMC material was produced by adding 3% wt SiC, with 40 \ua mean particle size, into 7075 aluminum alloy. In order to bond MMC materials a diffusion welding machine was designed and manufactured. Samples were cut and bonded by diffusion welding method with and without copper and silver interlayers. Bonded samples were cut trough the welding zone perpendicular to the welding interface. Mierostructure investigation and chemical analyses of the welding interface were conducted by using SEM and EDS. Microhardness and shear tests were carried out to check the mechanical properties of the bonded samples. A shear test apparatus was also designed and manufactured to employ in this study. Shear test results obtain from the matrix material, composite material and bonded samples, were compare to each other. Optical microscope studies on composites indicated that mierostructure of the composite was homogeneous and contained a small amount of porosity. Microhardness test result indicated a small amount of change in hardnesses of matrix material, composites material and bonded material. Copper interlayer has given higher hardness than that was seen on silver interlayed materials.EDS analysis showed that the diffusion distance in the welding with silver inteiiayer was longer than that was seen on the samle had copper interlayer. It was found that bonding of silver interlayer had higher shear resistance than that bonded with copper interlayer. However, the highest shear resistance was obtained on the sample bonded without interlayer. Science code : 6261901

Benzer Tezler

  1. Tez No

    152911

    %3 ve %5 SiC partikül takviyeli 7075 alüminyum alaşımı matrisli kompozitlerin yaşlandırma süresinin mekanik özelliklere etkisi

    Effect on mechanical properties of the aging period of 7075 aluminum alloy matrix composites with %3 and %5 SiC particulate reinforced

    PINAR UYAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2004

    Metalurji MühendisliğiEskişehir Osmangazi Üniversitesi

    Metalurji Mühendisliği Ana Bilim Dalı

    PROF.DR. REMZİ GÜRLER

  2. Tez No

    169215

    SiC parçacık takviyeli Al matris kompozit malzemelerin mekanik ve mikroyapı özelliklerine karıştırıcıtipive takviye oranı etkisinin incelenmesi

    Investigation of the effect of mixer type and SiC particle ratio on mechanical and microstructural properties of SiC particle reinforced Al matrix composites

    AHMET KÖKEN

    Yüksek Lisans

    Türkçe

    Türkçe

    2005

    Makine MühendisliğiDumlupınar Üniversitesi

    Makine Eğitimi Ana Bilim Dalı

    Y.DOÇ.DR. MUSTAFA AYDIN

  3. Tez No

    78498

    SİC seramik partikül takviyeli etial-195 aluminyum alaşımına argon kaynağı uygulaması

    Argon welding of SİC reinforced etial-195 metal matriks composite

    MUAZZEZ ÖNER

    Yüksek Lisans

    Türkçe

    Türkçe

    1998

    Metalurji MühendisliğiEskişehir Osmangazi Üniversitesi

    Metalurji Mühendisliği Ana Bilim Dalı

    DOÇ. DR. REMZİ GÜRLER

  4. Tez No

    152053

    Investigation of quasi-static and dynamic mechanical properties of functionally graded SiC-particulate reinforced aluminum metal matrix composites

    Fonksiyonel dereceli SiC parçacık takviyeli alüminyum metal matris kompozitlerin statik ve dinamik özelliklerinin incelenmesi

    UYGAR YILDIRIM

    Yüksek Lisans

    İngilizce

    İngilizce

    2004

    Makine Mühendisliğiİzmir Yüksek Teknoloji Enstitüsü

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MUSTAFA GÜDEN

  5. Tez No

    176905

    Assessment and modelling of particle clustering in cast aluminum matrix composites

    Döküm yoluyla üretilmiş alüminyum tabanlı kompozitlerde parçacık topaklanmasının değerlendirilmesi ve modellemesi

    ARDA ÇETİN

    Doktora

    İngilizce

    İngilizce

    2008

    Metalurji MühendisliğiOrta Doğu Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. ALİ KALKANLI

Geri Dön