The Effect of microstructure on wear resistance of M.K.E.K. Ç5190 steel
Başlık çevirisi mevcut değil.
- Tez No: 1312
- Danışmanlar: DOÇ. DR. HALUK ATALA
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: M.K.E.K. Ç 5190 çeliği, ostenitleme sıcaklıkları, karbürler, aşınma direnci. - vı, Aşınma dayanımı, Karbür, Çelik-metal, M.K.E.K. Ç 5190 steel, austenitizing temperatures, carbides, wear resistance. IV, Wear resistance, Carbide, Steel-metal
- Yıl: 1987
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Belirtilmemiş.
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET M.K.E.K. Ç 5190 ÇELÎGİNÎN AŞINMA DİRENCİNDE MIKROYAPININ ETKİSİ BAYSAN, Kâzım Yüksek Lisans Tezi, Metalürji Müh. Bölümü Tez Yöneticisi: Doç. Dr. Halûk ATALA Eylül 1987, 77 Sayfa Bu tez çalışmasında, M.K.E.K. Ç 5190 çeliği nin ostenitleme sıcaklığı araştırıldı. Tavlanmış durumdaki numunelere, değişik ostenitleme sıcaklıkla rında yağda su verme işlemi uygulanarak mikroyapı incelemesi, karbür sayımı ve büyüklüğü hesaplamaları yapıldı. Metalografik incelemeler Tarama Elekron Mik roskobu kullanılarak gerçekleştirildi. Ayrıca farklı ostenitleme sıcaklıklarında yağda su verilmiş numune lerin, laboratuvar şartlarında kuru sürtünmeli aşınma direnci testi uygulandı. Bu çalışmada, ostenitleme sıcaklığının 800 C civarında olduğu saptandı. Mikroyapmm marten- sit, çözünmemiş karbür ve kalıntı ostenitten oluştuğu gözlendi. - vOstenitleme sıcaklığının artmasıyla birlik te, çözünmemiş karbür miktarının azaldığı, fakat ka lıntı ostenit miktarının arttığı gözlendi. Aşınma direncinin maksimum olduğu ostenitieme sıcaklığı 840 °C olarak bulundu.
Özet (Çeviri)
ABSTRACT THE EFFECT OF MICROSTRUCTURE ON WEAR RESISTANCE OF M.K.E.K. Ç 5190 STEEL BAYSAN, Kâzım M.Sc. in Metallurgical Engineering Supervisor: Assoc. Prof. Dr. Haluk ATALA September 19 87, 77 Pages In this thesis > the austenitizing tempera ture of the M.K.E.K.- Ç 5190 steel was studied. The microstructure examination, carbide counting and sizing were performed on the specimens which are in the annealed condition, by quenching from various austenitizing temperatures in oil. The metallographic examinations were done by using Scanning Electron Microscope? In addition, a dry-sliding wear resistance test was applied to the specimens which were quenched in oil from different austenitizing tempe ratures in" laboratory conditions. In this study the austenitizing temperature was determined to be approximately 800 °C. It was observed that the microstructure consists of martens ite, undis solved carbide and retained austenite. - iii -It was observed that as the austenitizing temperature increases^ undissolved carbide amount decreases but retained austenite amount increases. It was also determined that the wear resis tance is maximum at the austenitizing temperature of 840°C.
Benzer Tezler
- Alüminanın özelliklerine, şekillendirme yönteminin, katkıların ve sinterleme sıcaklığının etkisi
The Effects of forming methods, additives and sintering temperature on the properties of the alumina ceramics
YÜKSEL PALACI
- Manganez bronzlarında ısıl işlemle sertleşme mekanizması ve faz dönüşümleri
The Phase transformation and hardening mechanism by heat treatment of cast manganese bronzes
ABDULLAH OTUZBİR
- Metal infiltre edilmiş mikro poroz karbon kompozitlerin aşınma ve sürtünme davranışının karakterizasyonu
Başlık çevirisi yok
GÜLTEKİN GÖLLER
Doktora
Türkçe
1997
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
PROF. DR. ADNAN TEKİN
- Kaynak edilebilen kobalt ve demir esaslı alaşımların yüksek sıcaklıkdaki aşınma davranışları
High temperature wear behaviour of weldable cobalt and iron based alloys
HALİS ÇELİK
- Çeliklerin ısı iletim katsayısının belirlenmesi
Determination of the thermal condictivities of the steels
BUKET YARDIMCI