Fe-%30 Ni-%0.2 Mn alaşımında soğutma etkisiyle elde edilen martensitik dönüşümlerin mössbauer spektroskopisi ve taramalı elektron mikroskobu (S.E.M) ile incelenmesi
Investigation of martensitic phase transformations which are formed by cooling effect in Fe-%30 Ni-%0.2 Mn alloy with using mössbauer spectroscopy and scanning electron microscope (S.E.M)
- Tez No: 127412
- Danışmanlar: Y.DOÇ.DR. ABDULLAH AYDIN
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: Austenite-Martensite, Mössbauer Spektroskopisi, Taramalı Elektron Mikroskobu ( SEM ), korner Kayma &&&, Martensit, Martensitik dönüşüm, Mikroskopi-elektron taramalı, Östenit, Austenite-Martensite, Mössbauer Spectroscopy, Scanning Electron Microscope ( SEM ), Isomer Shift, Martensite, Martensitic transformation, Microscopy-electron scanning, Austenite
- Yıl: 2002
- Dil: Türkçe
- Üniversite: Kırıkkale Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET Fe-%30Ni- % 0.2Mn ALAŞIMINDA SOĞUTMA ETKİSİYLE ELDE EDİLEN MARTENSİTİK FAZ DÖNÜŞÜMLERİNİN MÖSSBAUER SPEKTROSKOPİSİ VE TARAMALI ELEKTRON MİKROSKOBU (S.E.M) İLE İNCELENMESİ GÜLER, Emre Kırıkkale Üniversitesi Fen Bilimleri Enstitüsü Fizik Anabilim Dalı, Yüksek Lisans Tezi Danışman : Yrd. Doç. Dr. Abdullah Aydın Ocak 2002, 65 sayfa Bu tez çalışmasında, Fe -%30Ni-%0.2Mn alaşımında soğutma etkisi ile oluşturulan Martensitik faz dönüşümleri, Mössbauer Spektroskopisi ve Taramalı Elektron Mikroskobu (S.E.M) kullanılarak incelenmiştir. Elde edilen Mössbauer spektrumunda Fe -%30Ni-%0.2Mn alaşımının paramanyetik özellikteki austenite (ana) fazının tek pike, ferromanyetik özellikteki martensite (ürün) fazının ise 6 pike sahip olduğu gözlendi. Martensite fazın iç manyetik alanının değeri 33.8 T olarak ölçüldü ve her iki yapının izomer kayma değerleri de sırasıyla, -0.107 mm/sn ve -0.061 mm/sn olarak belirlendi.
Özet (Çeviri)
ABSTRACT INVESTIGATION OF MARTENSITIC PHASE TRANSFORMATIONS WHICH ARE FORMED BY COOLING EFFECT IN Fe -%30Ni-%0.2Mn ALLOY WITH USING MÖSSBAUER SPECTROSCOPY AND SCANNING ELECTRON MICROSCOPE ( SEM ) GÜLER, Emre Kırıkkale University Graduate School of Natural and Applied Sciences Department of Physics, M. Sc. Thesis Supervisor : Asst. Prof. Dr. Abdullah Aydın January 2002, 65 pages In this thesis study, martensitic phase transformations which are formed by cooling effect in Fe %30 Ni %0.2 Mn alloy are investigated with Mössbauer Spectroscopy and Scanning Electron Microscope ( SEM ). The single peak of the paramagnetic phase and the six peaks of the ferromagnetic phase of the Fe -%30Ni-%0.2Mn alloy was observed in the Mössbauer spectrum. The internal magnetic field strength of ferromagnetic martensite phase was determined as 33.8 T and the isomer shift values was determined as respectively -0.107 mm/sn and -0.061 mm/sn for two phase.
Benzer Tezler
- Yaş yöntemle üretilen fosforik asidin füzel yağlarıyla arıtılması üzerine bir çalışma
An Investigation on the purification of wet process phosphoric acid by fusel oil extraction
ITIR AY
- Atık pillerin değerlendirilmesi
Recyling used batteries
HANİFE BANABAK
Yüksek Lisans
Türkçe
1997
Kimya Mühendisliğiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. A. NURSEN İPEKOĞLU
- B2 O3 katkısının doğrudan sinterlenen isatropik sert ferritlerin manyetik özellikleri üzerine etkisi
Effect of B2 O3 addition on the magnetic propertiesof direct sintered isotropic hard ferrites
ALMİLA AK YILDIRIM
- Yenifoça-Aliağa bölgesi'nden alınan su ve sediment örneklerinde ve bu bölgede yayılış gösteren bir omurgasız ve bir alg türünde bazı ağır metal konsatrasyonlarının belirlenmesi
Determining some heavy metal concentrations in water and sediment samples taken from Yenifoça-Aliağa area and on an invertebrate and an alga species which tend to live in this area
HÜLYA CAN
- Karbotermik ferrobor üretim parametrelerinin optimizasyonu
The optimization of parameters for the carbothermic production of ferroboron
ONURALP YÜCEL