Mekanik alaşımlamanın volfram ağır alaşımlarının yüksek sıcaklık sinterleme davranışlarına olan etkilerinin incelenmesi

Investigations of mechanical alloying effect on high temperature sintering behaviors of tungsten heavy alloys

  1. Tez No: 126751
  2. Yazar: MERT CANARAN
  3. Danışmanlar: PROF. DR. M. LÜTFİ ÖVEÇOĞLU
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Alaşımlar, Mekanik alaşımlama tekniği, Sinterleme, Toz metalurjisi, Tungsten, Yüksek sıcaklık, Üretim yöntemleri, Alloys, Mechanical alloying technique, Sintering, Powder metallurgy, Tungsten, High temperature, Production methods
  7. Yıl: 2002
  8. Dil: Türkçe
  9. Üniversite: İstanbul Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Seramik Sanat Dalı
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

MEKANİK ALAŞIMLAMANIN VOLFRAM AĞIR ALAŞIMLARININ YÜKSEK SICAKLIK SİNTERLEME DAVRANIŞLARINA OLAN ETKİLERİNİN İNCELENMESİ ÖZET Bu yüksek lisans tezinde, elemental tozlardan yola çıkarak W-Ni-Fe üçlü sistemindeki 56Ni-24Fe-20W bileşimi atritör ortamında 10, 20, 30, 40 ve 50 saat süreyle mekanik olarak alaşımlanmıştır. Elde edilen bu mekanik alaşımlanmış yapıya hedef 90W7Ni3Fe bileşimini oluşturacak şekilde başlangıç W tozu ilavesi yapılmıştır. Elde edilen bu 90W7Ni3Fe bileşimindeki bu karışımlar 150 MPa'da preslendikten sonra 1460°C ve 1500°C'da sinterlenmişlerdir. İkinci bir paralel set olarak 50 saat atritör ortamında mekanik alaşımlanan 56Ni-24Fe-20W bileşimindeki tozdan hareketle yine başlangıç W tozu ilavesiyle 75W-80W-85W-90W-95W-(7/3 Ni:Fe) bileşimleri hazırlanmıştır. Tüm bu bileşimler de 150 MPa'da preslendikten sonra 1500°C'dasinterIenmiştir. Yapılan bu deneysel çalışmalar; atritörde mekanik alaşımlanan tozların taramalı elektron mikroskobu (SEM)'de gerçekleştirilen mikroyapı incelemeleri, dilatometre çalışmaları,, numunelerin boyutlarına göre yaş yoğunluk, Arşimed prensibine göre sinterlenmiş yoğunluk ölçümleri, optik mikroskobi ve sertlik ölçümleriyle desteklenen karakterizasyon çalışmasıyla desteklenmiştir. Mekanik alaşımlama işlemiyle zamana bağlı olarak mikroyapısal incelme ve homojenizasyon tespit edilmiştir. Fakat mekanik alaşımlanan bu yapıların 1500°C gibi yüksek bir sinterleme sıcaklığında sinterlenmesi durumunda tüm numunelerin aralarındaki başlangıç farklılıklarını ortadan kaldıran ve benzer özellik gösteren mikroyapılar elde edilmiştir. Bu amaçla dilatometre çalışmaları sonucunda seçilen 1460°C sıcaklığında ldk., 10dk., 30dk. ve 60 dk'lık sürelerle gerçekleştirilen sinterleme işlemi zamana ve mekanik alaşımlama süresine bağlı olarak mikroyapısal farklılıkları ortaya koymuş olup aynı sinterleme sıcaklığında daha düşük volfram tane boyutuna ve daha yüksek sertliğe sahip volfram ağır alaşımlarının üretilebileceğinin işaretini vermiştir. xı

Özet (Çeviri)

INVESTIGATIONS OF MECHANICAL ALLOYING EFFECT ON HIGH TEMPERATURE SINTERING BEHAVIORS OF TUNGSTEN HEAVY ALLOYS SUMMARY In this presented thesis, the comparative high temperature sintering behaviour of different composition of mechanically alloyed ternary W-Ni-Fe systems were investigated. In order to achieve this, preblended powder mixture constituting the composition of 56Ni-24Fe-20W was mechanically alloyed in an attritor mill for 10, 20, 30, 40, 50 hours. The mechanically alloyed composition was used for preparation of 90W7Ni3Fe heavy alloy mixtures by the addition of initial W powder. Resultant powder mixtures were compacted into cylindrical shapes under 150 MPa and sintered at 1460°C and 1500°C under a protective athmosphere. A second experimental set was also prepared for 50 hours mechanically alloyed powder mixture to obtain the target compositions of 75W-80W-85W-90W-95W-(7/3 Ni:Fe) heavy alloys. In the experimental studies; scanning electron microscopy (SEM) observations of mechanical alloyed powders were carried out, dilatometric studies were performed from the compacted powders, density measurements were also performed according to Archimedes Principles, optical microscopy observations were realized from the polished sample surfaces and hardness values were also measured in order to characterize the processing effects. Microstructural homogenization and fineness were obtained with the increasing of the mechanical alloying time. In the case of selection relatively high sintering temperature like 1500°C, all compositions were showed nearly similar microstructural features as a result of normalization effect. For this reason lower sintering temperature of 1460°C were selected after careful investigation of dilatometric studies and kinetic sintering experiment realized for duration of 1 min., 10 min., 30 min. and 60 min. This experiment was showed clear microstructural differences and we believe that this is a good sign for the lower temperature sintering production of tungsten heavy alloys with smaller tungsten grain sizes and better mechanical properties. xn

Benzer Tezler

  1. Tez No

    127122

    W-Ni-B ve W-Ni ağır alaşımlarının karşılaştırmalı sinterleme davranışları

    The Comparative sintering behaviours of W-Ni-B and W-Ni heavy alloys

    PINAR TURAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2002

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji Mühendisliği Ana Bilim Dalı

    PROF. DR. M. LÜTFİ ÖVEÇOĞLU

  2. Tez No

    139864

    Termomekanik proseslerin demir ve demir dışı malzemelere endüstriyel uygulamaları ve CuZn37 alaşımı üzerinde deneysel bir çalışması

    The Industrial application of thermomechanical process in ferrous non-ferrous metals and experimental study of CuZn37 alloy

    TUNÇ YÜKSEL

    Yüksek Lisans

    Türkçe

    Türkçe

    2003

    Metalurji MühendisliğiYıldız Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. ADEM BAKKALOĞLU

  3. Tez No

    185396

    FeMnSi alaşımlarının mekanik ve termal etkiler altında şekil hatırlama özelliklerinin incelenmesi

    Investigation of shape memory properties of FeMnSi alloys under mechanical and thermal effects

    MURAT ESKİL

    Doktora

    Türkçe

    Türkçe

    2006

    Fizik ve Fizik MühendisliğiFırat Üniversitesi

    Fizik Ana Bilim Dalı

    PROF. DR. MEHMET CEYLAN

  4. Tez No

    79249

    Haddelenmiş alüminyum bakır alaşımlarının mekanik ve korozyon özelliklerinin incelenmesi

    Başlık çevirisi yok

    HAKAN AKAR

    Yüksek Lisans

    Türkçe

    Türkçe

    1998

    Makine MühendisliğiYıldız Teknik Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ. DR. AYŞEGÜL AKDOĞAN

  5. Tez No

    18157

    Döküm dolgularda kullanılan değişik metal alaşımlarının mekanik ve elektrokimyasal özellikleri yönünden birbirleriyle karşılaştırılması

    Başlık çevirisi yok

    YAVUZ GÖMEÇ

    Doktora

    Türkçe

    Türkçe

    1990

    Diş Hekimliğiİstanbul Üniversitesi

    Diş Hastalıkları ve Tedavisi Ana Bilim Dalı

    PROF.DR. HİKMET ÇAMLI

Geri Dön