Sentetik vollastonit üretimi ve sır yapımında kullanılabilirliğinin araştırılması
The Investigation on producing synthetic wollastonite and its usage potential in glaze making
- Tez No: 123519
- Danışmanlar: YRD. DOÇ. DR. ALİ KARTAL
- Tez Türü: Yüksek Lisans
- Konular: Seramik Mühendisliği, Ceramic Engineering
- Anahtar Kelimeler: Karakterizasyon, Sinterleme, Sır, Volastonit, Characterization, Sintering, Glaze, Wollastonite
- Yıl: 2002
- Dil: Türkçe
- Üniversite: Afyon Kocatepe Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Seramik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Ill ÖZET SENTETİK VOLLASTONÎT ÜRETİMİ VE SIR YAPIMINDA KULLANILABİLİRLİĞİNİN ARAŞTIRILMASI Süleyman AKPINAR Seramik Ana Bilim Dalı Afyon Kocatepe Üniversitesi Fen Bilimleri Enstitüsü Haziran 2002 Danışman: Yrd. Doç. Dr. Ali KARTAL Bu çalışmada, sentetik olarak üretilen vollastonit ticari bir doğal vollastonit ile birlikte baz sır olarak belirlenen bir sır bileşimine değişen oranlarda ilave edilmesi ile hazırlanan sır kompozisyonlarının laboratuar koşullarında işletme karolarına aplike edilmesi ve pişirilmesi neticesinde elde edilen nihai ürünler üzerinde standartlar dahilinde yapılan testler ile vollastonit katkılarının sırın teknik özellikleri üzerindeki etkileri karşılaştırılmak suretiyle sentetik vollastonitin sır bünyesinde kullanılabilirliği araştırılmıştır. Deneysel çalışmalar üç aşamadan oluşmaktadır. Birinci aşamada, vollastonit sentezi ve karakterizasyonu gerçekleştirilmiştir. İkinci aşamada, baz sır kompozisyonu oluşturma ve bu sır kompozisyonunun erime sıcaklığının belirlenmesi çalışmaları gerçekleştirilmiştir. Üçüncü aşamada, baz sır kompozisyonuna değişen oranlarda (% 0, 5, 10, 15, 20) ayrı ayrı sentetik ve ticari doğal vollastonit katkıları yapılarak baz sırın erime sıcaklığında yapılan pişirim işlemi neticesinde elde edilen sırlı numuneler Harkort, aşınma dayanımı, kimyasallara dayanım, erime davranışlarının tespiti ve optik mikroskop testleri ile teknik özellikleri tespit edilmiştir. Sonuç olarak, sentetik ve doğal vollastonitin aynı CS fazlarım içerdiği, benzer erime davranışlarına sahip olduğu, sentetik vollastonitin doğal vollastonite göre daha yüksek ısısal genleşme katsayısına sahip olduğu tespit edilmiştir. Diğer taraftan, vollastonit katkılarının, sırın erime sıcaklığını, aşınma ve ısısal şok dayanımı nı düşürdüğü, kimyasallara ve lekelenmeye karşı dayanımı arttırdığı belirlenmiştir.
Özet (Çeviri)
IV ABSTRACT THE INVESTIGATION ON PRODUCING SYNTHETIC WOLLASTONITE AND ITS USAGE POTENTIAL IN GLAZE MAKING Süleyman AKPINAR Department of Ceramics Afyon Kocatepe University, Institute of Natural Sciences June 2002 Advisor: Asst. Prof. Dr. Ali KARTAL In this investigation, synthetic and natural wollastonite were added to a base glaze formulation at various proportions. The prepared glazes were applied to the factory's tiles and fired in the laboratory conditions. The technical properties of the final samples were characterised by standard tests. Experimental studies were conducted at three steps: In the first step, synthesising and characterising of wollastonite were performed. In the second step, making base glaze and determining of critical sintering temperature were done. In the third step, the final samples were tested in terms of the wearing and thermal shock resistance and staining resistance. At the end of this investigation, it was found that both type of wollastonite were consisted of the same CaO.Si02 (CS) phase, their melting behaviour were alike, the thermal expansion of synthetic wollastonite was higher than that of natural wollastonite. On the other hand, it was observed that the additional wollastonite reduced melting temperature of the base glaze, resistance of wearing and thermal shock but it increased resistance of chemical durability and staining.
Benzer Tezler
- B2O3 katkısının sentetik volastonit üretimi üzerine etkilerinin araştırılması
Researching the effects of B2O3 addition on synthetic vollastonite production
MURADİYE AĞAOĞLU
Yüksek Lisans
Türkçe
2006
Seramik MühendisliğiAfyon Kocatepe ÜniversitesiSeramik Mühendisliği Ana Bilim Dalı
DOÇ. DR. ALİ KARTAL
- CaCO3-SiO2 karışımlarından sentetik volastonit üretimi
The Production of synthetic wollastonite by mixture of CaCO3-SiO2
ALPASLAN KARA
Yüksek Lisans
Türkçe
2001
Seramik MühendisliğiAnadolu ÜniversitesiSeramik Mühendisliği Ana Bilim Dalı
DOÇ. DR. FERHAT KARA
- Volastonit minerali içeren anortit bazlı vitrifiye seramiklerin doğrudan hammaddelerden başlanılarak asıltı döküm yöntemi ile şekillendirilmesi
Slip casting of anorthite based vitrified ceramics containing wollastonite mineral starting directly from raw materials
TÜLİN ÇETİN
Yüksek Lisans
Türkçe
2002
Metalurji MühendisliğiGebze Yüksek Teknoloji EnstitüsüMalzeme Bilimi ve Makine Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. AHMET ÇAPOĞLU
- Influence of B2O3 addition on the microstructure of mica based glass-ceramics
B2O3 ilavesinin mika bazlı cam seramiklerin mikro yapısı üzerine etkileri
HAKAN AYKUT
Yüksek Lisans
İngilizce
2005
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ABDULLAH ÖZTÜRK
- Sentetik şelitin hidroklorik asit ortamındaki liçine karışık-sulu (HCl-C2H5OH-H2O) ve karışık-susuz (HCl-C2H5OH) çözücü sistemlerinin etkisi
Başlık çevirisi yok
SELAMİ ÖZDEMİR
Yüksek Lisans
Türkçe
1988
Metalurji MühendisliğiHacettepe ÜniversitesiMaden Mühendisliği Ana Bilim Dalı
DOÇ. DR. İSMAİL GİRGİN