Biyobozunur modifiye-nişasta/ polikaprolakton blendlerinin eldesi ve degredasyonu
Preparation of biodegradable modified-starch/ polycaprolactone blends and their degradation
- Tez No: 123434
- Danışmanlar: DR. HÜLYA YAVUZ
- Tez Türü: Yüksek Lisans
- Konular: Biyomühendislik, Bioengineering
- Anahtar Kelimeler: modifiye nişasta, polikaprolakton, degredasyon, Pseudomonas putida, aktif çamur, Bozunma, Nişasta, Modified starch, poly(e-caprolactone), degradation, Pseudomonas putida, active sludge, Activated sludge, Decomposition, Starch, Polycaprolactone
- Yıl: 2002
- Dil: Türkçe
- Üniversite: Hacettepe Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Biyomühendislik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Çevresel bilincin hızla artması ile biyobozunur polimerlerin kullanımı da önemli derecede arttırmıştır. Sunulan çalışmanın amacı; nişasta/poli(e-kaprolakton) filmlerinin hazırlanması ve çeşitli ortamlarda biyodegredasyonunun incelenmesidir. Çalışmanın ilk bölümünde, Poli(e-kaprolakton) (PCL) yığın polimerizasyonuyla, azot atmosferinde, katalizör olarak kalay oktoat kullanılarak sentezlenmiştir. Nişasta granüllerinin yüzey hidrofobisitesini arttırmak için, tüsodyum trimetafosfat (TSTP) kimyasal modifikasyonda çapraz bağlayıcı olarak kullanılmıştır. 0.70 üm kalınlığındaki modifiye-nişasta/PCL (MOD/PCL) (% 50/50), doğal-nişasta/PCL (NON/PCL) (% 50/50) ve PCL (% 100) filmler çözücü döküm yöntemiyle hazırlanmıştır. Filmler incelendiğinde, PCL'na nişasta eklenmesiyle elastiktik modülünün arttığı, gerilme dayanımı ve kopma anında uzama değerlerinin ise düştüğü gözlenmiştir. Hidrofobik nişastanın PCL fazı içerisinde doğal nişastaya göre daha düzenli bir şekilde dağıtılabildiği SEM fotoğrafları ve mekanik testlerle gözlenmiştir. Çalışmanın ikinci bölümünde, filmlerin aerobik degredasyonu iki ayrı ortamda, Pseudomonas putida ve aktif çamur varlığında gerçekleştirilmiştir. Filmlerin degredasyon hızları, mekanik ve morfolojik özelliklerindeki değişimlerle izlenmiştir. Buna göre P. putida varlığında hemen hemen hiç değişmeyen degredasyon hızının aktif çamur varlığında önemli derecede arttığı bulunmuştur. Ayrıca beklendiği gibi nişasta içeren filmlerin degredasyonu polikaprolaktona göre daha hızlı olurken, modifiye nişastanın doğal nişastaya göre daha yavaş degrede olduğu gözlenmiştir.
Özet (Çeviri)
Rapid increase in environmental concern increased the use of biodegradable polymers considerably. Aim of this study is to prepare starch/polycaprolactone films and to investigate their biodegradation under aerobic environments. In the first part of the study, Poly-e-caprolactone (PCL) was synthesized by bulk polymerization by using stannous octoate as the catalyst under nitrogen environment. In order to increase the surface hydrophobicity of starch granules, trisodium trimetaphosphate (TSTP) was used as a crosslinking agent in chemical modification. 0.70 \xm thickness films were prepared from modified-starch/PCL (MOD/PCL) (50/50%), nonmodifıed-starch/PCL (NON/PCL) (50/50%) and PCL by using solvent-casting method. Investigation of films implied that the addition of starch granules into PCL contributed to improve its modulus while depressing the shear stress and elongation at break values. Dispersion of hydrophobic starch in PCL phase was more uniform compared to natural starch which was observed by SEM and mechanical tests. In the second part of the study, aerobic degradation of films were followed under two different environments; in the presence of Pseudomonas putida and activated sludge. Degradation rate of films were monitored by the change in mechanical and morphological properties. It was observed that while the presence of Pseudomonas putida having no effect on degradation rate, activated sludge accelerated the degradation rate considerably. It was also observed that as expected the degradation rate of starch containing films were higher that of polycaprolactone while degradation rate of modified starch was slower than the natural starch.
Benzer Tezler
- Üç-boyutlu, biyobozunur/biyobozunur olmayan polimerik taşıyıcıların biyosinyallerle plazma modifikasyonu ve hücre kültür uygulamaları
Plasma modification of 3D, biodegradable/nondegradable polymeric carriers by biosignals and their applications in cell culture
HİLAL TÜRKOĞLU ŞAŞMAZEL
Doktora
Türkçe
2007
BiyomühendislikHacettepe ÜniversitesiBiyomühendislik Ana Bilim Dalı
PROF.DR. MENEMŞE GÜMÜŞDERELİOĞLU
- Sentetik ve biyosentetik polimerlerle bazı vinil monomerlerinin blok/graft kopolimerlerinin hazırlanması
The syntheses of block/graft copolymers of synthetic and biosynthetic polymers with some vinyl monomers
HÜLYA MACİT
- Preparation and surface modification of suitable membranes to prevent the bioadhesion formation in surgical operations
Cerrahi uygulamalarda biyoadezyon oluşumunu engellemek üzere uygun membranların hazırlanması ve yüzeylerinin modifiye edilmesi
HASAN HÜSEYİN MURT
- Antibiotic release from biodegradable microbial polyesters
Biyobozunur mikrobiyal poliesterleren antibiyotik salımı
DİLEK ŞENDİL
Yüksek Lisans
İngilizce
1997
Bilim ve TeknolojiOrta Doğu Teknik ÜniversitesiBiyoteknoloji Ana Bilim Dalı
PROF. DR. VASIF NEJAT HASIRCI
- Properties of biodegredable and compatible poly (3-hydroxybutyrak) and its copolymers
Biyobozunur ve biyouyuşumlu poli (3-hidroksi bufirat) ve kopolimerlerinin özellikleri
MUSTAFA KEMAL ÖZ
Yüksek Lisans
İngilizce
1999
KimyaOrta Doğu Teknik ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. ERDAL BAYRAMLI