Bizmut tabanlı yüksek sıcaklık süperiletkenlerinin yabancı atom katkısıyla sentezlenmesi ve karakterizasyonları
Synthesis and characterizations of bizmut based high TC superconductors by substitution of foreign atoms
- Tez No: 120226
- Danışmanlar: PROF. DR. DOĞAN ABUKAY
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: BSCCO, Yüksek Sıcaklık Süperiletkenleri, K Katkısı, Katkı etkisi, Çift Atom Katkısı, Bizmut, Karakterizasyon, Sentez, Süper iletkenler, Yüksek sıcaklık, BSCCO, High Tc Superconductors, K Substitution, Effect of Doping, Co-doping, Bismuth, Characterization, Synthesis, Superconductors, High temperature
- Yıl: 2002
- Dil: Türkçe
- Üniversite: Ege Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
V ÖZET BİZMUT TABANLI YÜKSEK SICAKLIK SÜPERİLETKENLERİNİN YABANCI ATOM KATKISIYLA SENTEZLENMESİ VE KARAKTERİZASYONLARI DENÎZ,Coşkun Yüksek Lisans Tezi,Fizik Bölümü Tez Yöneticisi : Prof. Dr. Doğan ABUKAY Nisan 2002,49 sayfa Bu tezde“Bizmut tabanlı yüksek Sıcaklık Süperiletkenleri”ne yabancı atom katkılarının etkileri incelenmiştir.Bunun için Bi tabanlı 2223 fazındaki Yüksek Sıcaklık Süperiletken seramik yapılarına,Bi yerine Pb+Sb ve Sr yerine x=0.00,0.0 1,0.02,0.03 ve 0.04 oranlarında K katkısı yapılarak elde edilen Biı.6Pbo.3Sro.!Sr2-xKxCa2Cu30y yapısının süperiletkenlik özellikleri, Direnç-Sıcaklık, A.c. Magnetik Süseptibilite- Sıcaklık ve X-ışını kırınım desenleriyle incelenmiştir. Örnekler, geleneksel katıhal reaksiyon yöntemiyle ve karşılaştırmak üzere farklı tavlama sıcaklıklarıyla hazırlanmıştır. Örneklerden 850°C sıcaklıkta 192 saat tavlanan örneklerin, 835°C sıcaklıkta 120 saat tavlanan örneklere göre, yüksek Tc fazının oldukça kararlı olduğu, K katkısıyla birlikte süperiletken hale geçiş sıcaklığının yükseldiği ve geçişin daha keskin olduğu görüldü. K katkısı ile Bi tabanlı yüksek sıcaklık süperiletkenlerinin temel karakteristik parametrelerin artırılabileceği anlaşıldı. Burada K katkısının yapıdaki tanecikler arası zayıf bölgeyi güçlendirdiği düşünülmektedir.
Özet (Çeviri)
VII ABSTRACT SYNTHESIS OF BISMUTH BASED HIGH TEMPERATURE SUPERCONDUCTORS BY FOREIGN ATOM SUBSTITUTIONS AND THEIR CHARACTERIZATIONS DENİZ,Coşkun Msc.in Dept.of Physics Supervisor.Prof.Dr.Doğan ABUKAY April 2002,49 pages In this thesis,effects of foreign atom substitutions in“Bizmuth- based High Temperature Superconductors”have been studied. For this, superconducting properties of Biı.?Pbo.3Sro.ıSr2.xKxCa2Cu30y structure obtained by Pb+Sb substition for Bi and K substitition for Sr in the molar ratios of x=0.00,0.0 1,0.02,0.03 and 0.04 has been examined by means of Resitance-Temperature, A.C.magnetik susceptibility-Temperature measurements and X-Ray Diffraction patterns. Samples have been prepared by the familiar solid state reaction method in different synthesis temperatures for comparision. High Tc phases of the samples which synthesed at 850°C for 192 hours have been seen that having quite higher stabilization in the High Tc phase than those which synthesed at 835°C for 120 hours.Besides, by the substiitution of K superconducting state transition temperatures have been incresed and transitions have become sharper.lt has been understood that, fundamental characteristic parameters of Bi-based High Temperature Superconductors can be increased by means of K substitution.The role of K substitution has been considered to be strengthening the intergranular weak regions in the structure.
Benzer Tezler
- Effects of B2O3 addition on the formation and properties of bi-based superconductors
B2O3 eklemesinin bizmut tabanlı süperiletkenlerin yapısına ve özelliklerine etkileri
DEVRİM KÖSEOĞLU
Yüksek Lisans
İngilizce
2003
Fizik ve Fizik MühendisliğiOrta Doğu Teknik ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. HÜSNÜ ÖZKAN
PROF. DR. NİZAMİ HASANLİ
- Yüksek sıcaklık süperiletkenlere kaplama olarak kullanılan gümüş ve gümüş alaşımlarının magneto-dirençlerinin sıcaklık ve magnetik alana bağlı solarak değişimlerinin incelenmesi
Başlık çevirisi yok
OSMAN DUR
Doktora
Türkçe
1998
Fizik ve Fizik MühendisliğiMarmara ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. ÖMER ASIM SAÇLI
- Ekran baskı yöntemi ile elde edilen Bi2-xPbxSr2Ca2Cu3O10+y üstüniletken kalın filmlerin galvanomagnetik özellikleri
Başlık çevirisi yok
ERTAN ŞAHİN
Yüksek Lisans
Türkçe
1996
Fizik ve Fizik MühendisliğiHacettepe ÜniversitesiFizik Ana Bilim Dalı
DOÇ.DR. NECDET BAŞTÜRK
- Synthesis and structural characterization of the Bi-based superconductors
Bizmut içeren süperiletkenlerin sentezi ve yapısal karakterizasyonu
ALAAEDEEN ABUZIR
Yüksek Lisans
İngilizce
2000
Fizik ve Fizik MühendisliğiOrta Doğu Teknik ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. HÜSNÜ ÖZKAN
- Bi-Sn, Bi-Pb ve Bi1-xSbx yarımetal alaşımlarında ultrasonik ve galvanomagnetik ölçümler
Başlık çevirisi yok
KIVILCIM KILIÇ