A Study on flexural strength of layered Al-SiCp composites produced by powder metallurgy methods

Monolitik ve katmanlı Al-SiCp kompozitlerin eğme dayanımı

  1. Tez No: 119070
  2. Yazar: SÜHA TİRKEŞ
  3. Danışmanlar: PROF. DR. BİLGEHAN ÖGEL, DOÇ. DR. RIZA GÜRBÜZ
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Eğme dayancı, çekiç düşürme testi, düşük hız balistiği, metal matris kompozitler, AI-SiC, Alüminyum alaşımları, Eğilme dayanımı, Karbon, Kompozitler, Flexural Strength, Drop-Weight Test, Low velocity ballistic limit, MMC, Ai-SiC. T.C YÛKSEKtoKEHM KUSULO iv nmcündANT*sv«« MRRKHİ, Aluminum alloys, Bending strength, Carbon, Composites
  7. Yıl: 2002
  8. Dil: İngilizce
  9. Üniversite: Orta Doğu Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

öz MONOLİTİK VE KATMANLI AI-SiCp KOMPOZİTLERİN EĞME DAYANIMI Tirkeş, Süha Yüksek Lisans, Metalürji ve Malzeme Bölümü Tez Yöneticisi: Prof. Dr. Bilgehan ÖGEL Ortak Tez Yöneticisi: Assoc. Prof. Dr. Rıza GÜRBÜZ Aralık 2002, 73 sayfa AI-SiC kompozitleri Aı (ort. 26.2jj,m), Cu (ort. 63(a.m) ve SiC tozlarının karışımından üretilmiştir. Kuvvetlendirici parçacık boyutunun etkisini araştırmak için ortalama 10|a.m ve 40jo,m parçacık boyutunda SiC kullanılmıştır. 30mm x 40mm x 5mm boyutunda numuneler nitrojen altında sıcak pressleme ile üretilmiştir. Bu çalışmadaki kompozitler ağırlıkça10%SiC ve 30%SiC den oluşmaktadır. Çift-katmanlı numuneler AI-10%SiC ve Al- 30%SiC katmanlarından oluşmaktadır. 150°C de yaşlandırma işleminden sonra monolitik ve çift-katmanlı numunelerin eğme dayançları araştırılmıştır. Bir çok numuneninde çekiç-düşürme testi kullanılarak düşük hızda darbeye karşı davranışları belirlenmiştir.Her iki 10%SiC ve 30%SiC için AI-SiC(40>m) kompozitieri Al-SiC(IO^m) kompozitlerine göre daha yüksek eğme dayana göstermişlerdir. Çift- katmanlı kompozitlerin eğme dayançları monolitiklerininkilerle aynı aralıkdadır. Gerinim bölgesinde 10%SiC ya da 30%SiC olmasına bağlı olarak çift-katmanlı numunelerin dayancı gerinimdeki katmanın dayancı ile sınırlı olduğu tespit edilmiştir. Çekiç-düşürme testinde ise aynı kalınlıktaki monolitik numunelere gore çift katmanlı numuneler daha fazla direnç göstermişlerdir.

Özet (Çeviri)

ABSTRACT A STUDY ON FLEXURAL STRENGTH OF LAYERED Al-SiC COMPOSITES PRODUCED BY POWDER METALLURGY METHODS Tirkeş, Süha M.S. Department of Metallurgical and Materials Engineering Supervisor: Prof. Dr. Bilgehan ÖGEL Co-Supervisor: Assoc. Prof. Dr. Rıza GÜRBÜZ December 2002, 73 pages Al-SiC particulate reinforced composites were produced from a mixture of pure Al powder (avg. 26.2fj.rn), Cu powder (avg. 63p,m) and SiC powder. An average SiC powder size of 10 \xm and 40 p.m were used in all composites to investigate the effect of reinforcing particulate size. The hot consolidation of powders was carried out in a single-end rectangular die under nitrogen atmosphere to produce 30mm x 40mm x 5mm rectangular specimens. The composites in this study comprised either 10w/oSiC or 30w/oSiC. The bi-layer Al-SiC composites were produced in the form of AMOw/oSiC and AI-30w/oSiC two layer rectangular bars. After ageing at 150°C, the bend strength of monolithic and bi-layer composites were investigated. The low velocity impact 111behavior of several specimens was also determined using drop weight test apparatus. AI-SiCp(40jxm) composites have yielded higher flexural strength than the AI-SiC(10|^m) ones for both 10w/oSiC and 3Qw/oSiC. The flexural strength of bi-layer composites were in the range of monolithic ones. Depending on whether 10w/oSiC or 30w/oSiC layer is loaded in tension, the flexural strength of the bi-layer composite was very similar to that of monolithic composite with identical reinforcement content. In contrast to bend tests, the drop-weight test results have showed that bilayer composites have higher resistance to perforation when compared to the monolithic specimens of same thickness.

Benzer Tezler

  1. Tez No

    183483

    Mechanical and thermal properties of non-crimp glass fiber reinforced composites with silicate nanoparticule modified epoxy matrix

    Silika nanopartiküller ile modifiye edilmiş epoksi matriksli kıvrımsız fiber takviyeli kompozitlerin mekanik ve termal özellikleri

    EMRAH BOZKURT

    Yüksek Lisans

    İngilizce

    İngilizce

    2006

    Makine Mühendisliğiİzmir Yüksek Teknoloji Enstitüsü

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ.DR. METİN TANOĞLU

  2. Tez No

    14060

    Isıl işlem parametrelerinin hafif beton özeliklerine etkisi

    Influence of heat treatment parameters on properties of lighweight concrete

    MUSTAFA ERKAN KARAGÜLER

    Doktora

    Türkçe

    Türkçe

    1988

    İnşaat Mühendisliğiİstanbul Teknik Üniversitesi

    DOÇ.DR. MEHMET UYAN

  3. Tez No

    2184

    Alçı sünger taşı cam lifi kompoziti

    The Gypsum-pumice-glass fiber composite

    HALİT YAŞA ERSOY

    Doktora

    Türkçe

    Türkçe

    1985

    İnşaat Mühendisliğiİstanbul Teknik Üniversitesi

    PROF. DR. FERRUH KOCATAŞKIN

  4. Tez No

    196233

    Geçici kuron - köprü materyallerinin polietilen ve cam fiberle güçlendirilmesinin bükülme direncine etkisinin incelenmesi

    The evaluation of polyethylene miber and glass fiber reinforcement on flexural strenght of provisional crown-bridge materials

    RABİA KAVRUT

    Doktora

    Türkçe

    Türkçe

    2007

    Diş HekimliğiAtatürk Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF.DR. LÜTFÜ İHSAN ALADAĞ

  5. Tez No

    75924

    Effects of air entrainment on properties of concrete

    Hava sürüklemenin betonun özellikleri üzerindeki etkileri

    BAHADIR HALİM USLU

    Yüksek Lisans

    İngilizce

    İngilizce

    1998

    İnşaat MühendisliğiOrta Doğu Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DR. LÜTFULLAH TURANLI

Geri Dön