The Effect of microstructure and hardness on acoustic properties of hypoeutectoid plain-C steels
Mikroyapının ve sertliğin ötektoid-altı yalın karbon çeliklerinin akustik özelliklerine etkisi
- Tez No: 118916
- Danışmanlar: YRD. DOÇ. DR. C. HAKAN GÜR, PROF. DR. ERDOĞAN TEKİN
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Ötektoid altı yalın karbon çelikleri, ısıl işlem, ultrasonik dalga hızı, ses zayıflaması, sertlik, mikroyapı VI, Akustik özellikler, Karbon çeliği, Mikroyapı, Sıcak haddeleme, Hypoeutectoid plain-C steels, heat treatment, ultrasonic wave velocity, sound attenuation, hardness, microstructure IV, Acoustic properties, Carbon steel, Microstructure, Hot rolling
- Yıl: 2002
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
öz MIKROYAPININ VE SERTLİĞİN ÖTEKTOID-ALTI YALIN KARBON ÇELİKLERİNİN AKUSTİK ÖZELLİKLERİNE ETKİSİ Keleş.Yankı Yüksek Lisans Metalürji ve Malzeme Mühendisliği Bölümü Tez Yöneticisi: Yrd. Doç. Dr. C. Hakan GÜR Ortak Tez Yöneticisi: Prof. Dr. Erdoğan TEKİN Nisan 2002, 75 sayfa Bu tezde, yalın karbon çeliklerinin mikroyapı ve sertlik özellikleri ile ultrasonik ölçümler arasındaki ilişki araştırılmıştır. Bu amaçla, hem sıcak haddelenmiş durumda hem de çeşitli ısıl işlemlerden sonra SAE 1020, SAE 1030, SAE 1040 ve SAE 1050 çelik numunelerde sertlik ve doğrudan temas yöntemi ile ultrasonik ses hızı, ses zayıflaması ölçümleri yapılmıştır. Numuneler, 860°C, 960°C ve 1060°C'de 1,5 saat süre ile östenitlendikten sonra, farklı soğuma hızları elde etmek için fırında soğutma, havada soğutma ve yağda su verme işlemleri uygulanmıştır. Farklı frekansta çeşitli problar kullanılarak enine ve boyuna dalgaların ilerleme hızı ölçülmüştür. Arka duvar yankı yüksekliklerinin değişim eğrileri 10 MHz probla elde edilmiştir. Ultrasonik hız ve ses zayıflaması ölçümlerinden elde edilen sonuçlar, sertlik değerleri ve mikroyapı dikkate alınarak tartışılmıştır. Söz konusuçeliklerde, ses hızı ve ses zayıflama özelliklerinin mikroyapı ve sertlikten etkilendiği ve ilave araştırmalarla daha genel sonuçlara ulaşılabileceği anlaşılmıştır.
Özet (Çeviri)
ABSTRACT THE EFFECT OF MICROSTRUCTURE AND HARDNESS ON ACOUSTIC PROPERTIES OF HYPOEUTECTOID PLAIN-C STEELS Keleş.Yankı M.S. Department of Metallurgical and Materials Engineering Supervisor: Assist. Prof. Dr. C. Hakan GÜR Co-Supervisor: Prof. Dr. Erdoğan TEKİN April 2002, 75 pages The aim of the thesis is to establish a correlation between ultrasonic measurements and microstructural properties and hardness of plain-C steels. Ultrasonic wave velocity and sound attenuation by direct coupling method and hardness in SAE 1020, SAE 1030, SAE 1040 and SAE 1050 plain-C steels in the as-produced state and after various heat treatments were measured. After austenitizing the specimens at 860°C, 960°C and 1060°C for 1,5 hours, furnace cooling, normalizing and oil quenching was applied to obtain different cooling rates. Velocities of both longitudinal and transversal waves were measured using probes with various frequencies. Backwall echo patterns were obtained using a 10 MHz straight-beam probe. mThe results of ultrasonic velocity and attenuation measurements were discussed by comparing the hardness values and microstructure of the specimens. It was concluded that ultrasonic velocity and attenuation behaviour are affected by the hardness and microstructural constituents of the steels used, and further research is necessary to generalize these conclusions for all steels.
Benzer Tezler
- Eklemeli imalat destekli dereceli hassas döküm yöntemi ile bal peteği yapıların üretimi ve karakterizasyonu
Production and characterization of honeycomb structures by additive manufacturing-aided investment flask mould casting method
FATİH GÜLER
Yüksek Lisans
Türkçe
2019
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. ÖZGÜL KELEŞ
DR. LEVENT TURHAN
- Tarihi yapıların onarımına yönelik doğal taş tozu ile polimer bağlayıcılı harçların üretimi ve karakterizasyonu; Sille taşı örneği
Production and characterization of natural stone powder and polymer binding mortars for the repair of historic buildings; Sille stone example
AHMET CİHAT ARI
- The effect of temperıng on mıcrostructure and hardness of FE-1C-2si (wt%) AND Fe-1C-2Si-2Cu-1Ni (wt%) nanobaınıtıc steels
Menevişleme işleminin FE-1C-2si (wt%) ve Fe-1C-2Si-2Cu-1Ni (wt%) nanobeynitik çeliklerinin içyapı ve sertliği üzerindeki etkileri
ZEYNEP ÖZTÜRK TAŞ
Doktora
İngilizce
2025
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. BİLGEHAN ÖGEL
PROF. DR. ALİ KALKANLI
- Effect of heat treatment on the hardness, microstructure and wear resistance of cast FE-MN-AL-NI-C lightweight steel
Isıl işlemin döküm FE-MN-AL-NI-C hafif çeliğinin sertlik, içyapı ve aşınma direncine etkisi
CAN ZÜMRÜT
Yüksek Lisans
İngilizce
2025
Metalurji MühendisliğiAtılım ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. ERKAN KONCA