5 farklı dual-cure yapıştırıcı rezin simanın değişik kompozit ve porselen kalınlıkları altında polimerizasyon etkinliğinin karşılaştırılması
The influence of composite or ceramic inlay thickness on hardening of 5 different dual-cured resin luting cements
- Tez No: 115981
- Danışmanlar: PROF. DR. NUR EMEL HERSEK
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dual-cure rezin siman, inley/onley, laminate veneer, sertlik testleri, kimyasal ve ışıkla polimerizasyon, Dual-cure resin luting cement, chemically and light activation, microhardness test, composite or ceramic inlay / onlay, laminate veneers
- Yıl: 2002
- Dil: Türkçe
- Üniversite: Hacettepe Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protez Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
5 Farklı Dual-Cure Yapıştırıcı Rezin Simanın Değişik Kompozit ve Porselen Kalınlıkları Altında Polimerizasyon Etkinliğinin Karşılaştırılması. Hacettepe Üniversitesi Sağlık Bilimleri Enstitüsü Protez (Diş) Programı Doktora Tezi, Ankara, 2002. Dual-cure rezin simanlar hem kimyasal olarak hem de ışık aktivasyonu ile polimerize olurlar. Fakat klinik olarak simanın bütün yüzeylerine ışık kaynağı tam olarak ulaşamaz. Bu amaçla, çalışmamızda inley kalınlığının rezin simanın sertliğine ayrıca ışıksız ve ışıkla polimerizasyonun simanın sertleşme derecesine etkisi araştırılmıştır. Bunun için 5 farklı dual-cure rezin siman (3M Opal, Calibra, Nexus, Variolink II, Panavia-F) kullanılarak 8x1 mm boyutlarında her bir simandan 20 adet örnek hazırlanmıştır. Bu örneklerden 10 tanesi değişik kalınlıklardaki (1-5 mm) kompozit diskler aracılığıyla, diğer 10 tanesi ise değişik kalınlıklardaki porselen diskler aracılığıyla polimerize edilmiştir. Daha sonra bu siman örneklerin polimerizasyon etkinliğini değerlendirmek için 3 değişik zamanda(1 saat, 24 saat, 1 hafta) Knoop sertlik ölçümleri yapılmıştır. Ayrıca herbir simandan 4 adet örnek hazırlanmıştır. Bu örneklerden 2 tanesi ışık uygulanmadan kimyasal polimerizasyona bırakılmıştır. Diğerleri ise bir yüzeyinden ışık uygulanarak dual-cure polimerize edilmiştir. Daha sonra bu örneklerin 1 saat, 24 saat, 1 hafta sonraki Knoop sertlik ölçümleri yapılmıştır. Elde edilen sonuçlara göre kompozit ve porselen kalınlığı arttıkça polimerizasyon etkinliği azalmaktadır. Ayrıca çalışmanın 2. bölümüne göre ise kullanılan dual-cure rezin simanların kimyasal ve ışıkla aktivasyon özellikleri birbirlerinden oldukça farklı bulunmuştur. Buna göre bu simanların kimyasal polimerizasyonu tek başına yeterli değildir.
Özet (Çeviri)
The effect of composite or ceramic inlay thickness on hardening of 5 different dual-cured resin luting cements and comparison of chemical versus dual-curing of resin luting cements. Dual-cure resin luting cements polymerize both chemically and through light activation; however, clinically some aspects of the cement are not readily accessiable to the light source. This study investigated the effect of inlay thickness on cement hardness and the degree of cement hardening achieved through chemical curing only versus dual curing. Disks 8 x1 mm were prepared from five commercially available dual-cure resin luting cements (3M Opal, Calibra, Nexus, Variolink II, Panavia-F). 20 specimens were prepared from each cement. 10 specimens were dual-cured through resin composite spacers of varying thicknesses (1 to 5 mm) and the others were cured through similar ceramic spacers, and hardness measurements were then recorded at 1 hour, 24 hours, and 1 week intervals. In addition, four specimens were prepared from each material; half of the specimens were cured chemically only, and remainder were dual-cured. Knoop hardness measurements were recorded. Multivariate analysis of variance revealed significant difference in hardness of specimens dual-cured through ceramic or resin composite spacers 2 to 3 mm in thickness or more versus those that were dual-cured without spacer regardless of the spacer material. Significant difference were also found in the hardness of chemically cured versus dual-cured specimens at the % 5 level of significance for all examined cements.
Benzer Tezler
- Farklı tekniklerle hazırlanmış porselen laminate veneer kronların ve yapıştırma sistemlerinin fiziksel olarak değerlendirilmesi
A Physical evaluation of porcelain laminate veneer crowns and their bonding systems prepared with various techniques
MEHMET ALİ KILIÇARSLAN
Doktora
Türkçe
1997
Diş HekimliğiAnkara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ALİ ZAİMOĞLU
- Bir cam fiber post sisteminde post uzunluğunun, kırılma dayanımına ve fonksiyonel kuvvetler altında oluşan streslerin yayılımına etkisinin incelenmesi
Evaluation of the effect of post length on fracture resistance and stress distribution of a glass fiber post system under functional forces
NEJDET ADANIR
Doktora
Türkçe
2002
Diş HekimliğiSelçuk ÜniversitesiDiş Hastalıkları ve Tedavisi Ana Bilim Dalı
DOÇ.DR. SEMA BELLİ
- Porselen lamina veneerlerin marjinal uyumunun incelenmesi
Marginal adaptation of different veneer systems
ÇİĞDEM ÇELİK (KASAPOĞLU)
Doktora
Türkçe
1999
Diş HekimliğiMarmara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. DENİZ GEMALMAZ
- Farklı tekniklerle uygulanan kompozit inleylerin mikrosızıntı yönünden in vitro olarak incelenmesi
In vitro evaluation of microleakage around composite inlays fabricated by different techniques
YILDIRIM HAKAN BAĞIŞ
- Seramik laminant veneer restorasyonların in vitro ve in vivo değerlendirilmesi
In vitro and in vivo evaluation of ceramic laminate veneer restorations
BİLKAY EMRE KARAMAN
Doktora
Türkçe
2005
Diş HekimliğiEge ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF.DR. MÜBİN SITKI ULUSOY