Toz enjeksiyon kalıplama ile üretilmiş 17-4 çökeltiyle sertleştirilmiş paslanmaz çelik gaz ve su atomize toz parçalarının karakterizasyonu
Characterization of powder injection molded parts made from gas and water atomised 17-4 precipitation hardening stainless steel powder
- Tez No: 114800
- Danışmanlar: PROF. DR. SEDAT ÖZBİLEN
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Paslanmaz Çelikler, Toz Enjeksiyon Kalıplama, Karakterizasyon, Paslanmaz çelik, Stainless Steel, Powder Injection Moldinng, Characterisation Page Number : 90 Adviser : Prof. Dr. Sedat ÖZBİLEN, Characterization, Powder injection molding
- Yıl: 2001
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metal Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
TOZ ENJEKSİYON KALIPLAMA İLE ÜRETİLMİŞ 17-4 ÇÖKELTİYLE SERTLEŞTİRİLMİŞ PASLANMAZ ÇELİK GAZ VE SU ATOMİZE TOZ PARÇALARININ KARAKTERİZASYONU (Yüksek Lisans Tezi) Murat DALKBLINÇ GAZİ ÜNİVERSİTESİ FEN BİLİMLERİ ENSTİTÜSÜ Aralık 2001 ÖZET Bu çalışmada 17-4 PH (çökeltiyle sertleştirilmiş) paslanmaz çelik tozlarından metal toz enjeksiyon kalıplama (MTEK) yöntemiyle üretilen iş parçalarının karakterizasyonu yapıldı. Bunun için içerisinde ince (dm= 14 um) ve küresel gaz atomize 17-4 PH paslanmaz çelik tozları ile %0, 70, 80, 90 ve 100 oranında iri (dm= 23,3 fim) ve karmaşık şekilli su atomize 17-4 PH paslanmaz çelik tozları bulunan metal toz harmanına çok bileşenli balmumu-polimer esaslı bağlayıcı karışımı ilavesi ile elde edilen besleme stokları hazırlandı. Hazırlanan bu besleme stokları karıştırma, kalıplama, çözgen ve termal ayrıştırma metotları ile bağlayıcı giderme ve 1250, 1280, 1300 ve 1350°C sıcaklıklarında 1 ve 2 saat süreyle hidrojen atmosferinde sinterleme gibi klasik MTEK işlem sırasını takiben 1000°C de 1 saat süre ile argon gazı ortamında homojenize edildiler. Çözündürmeyi ( homojenize etme ) takiben yapılan buzlu suda su verme işlemi sonrası aynı numuneler 500 ve 550°C sıcaklıklarda 4 saat süre ile yine argon gazı ortamında yaşlandırma işlemine tabii tutuldular. Tüm bu işlemler sonucunda, üretilen 17-4 PH paslanmaz çelik MTEK iş parçaları, kullanılan başlangıç tozları, kalıplanmış ve bağlayıcıları giderilmiş numuneler, sinterlenmiş ve homojenize edilmiş numuneler ve yaşlandırılmış numuneler de dahil olmak üzere lazer toz-tane ebat ve ebat dağılımı, optik ve tarama elektron mikroskobu metallografik ve kırık yüzey analizleri, sertlik ölçümleri kombinasyonundan oluşan karakterizasyon yöntemleri kullanılarak detaylı bir şekilde incelendiler. Yapılan bu detaylı araştırma sonucunda sadece besleme stoğunun harmanlı toz bileşiminin değil, aynı zamanda bağlayıcı giderme metotları, sinterleme süre ve sıcaklıkları, homojenleme ve takibinde uygulanan yaşlandırma sıcaklıklarının üretilen 17-4 PH paslanmaz çelik MTEK iş parçalarında mikroyapı-özellikler ilişkilerine olan etkileri incelendi ve belirlendi.Bilim Kodu : 3.022
Özet (Çeviri)
Ill CHARACTERISATION OF POWDER INJECTION MOLDED PARTS MADE FROM GAS AND WATER ATOMISED 17-4 PRECIPITATION HARDENING STAINLESS STEEL POWDER (M.Sc. Thesis) Murat DALKILINÇ GAZİ UNIVERSITY INSTITUTE OF SCIENCE AND TECHNOLOGY December 2001 ABSTRACT In this study, the characterisation of 17-4 PH (precipitation hardening) stainless steel parts made by metal powder injection molding (MPIM) were carried out. For this purpose, feedstocks (compounding) containing a pre-determined multi- component wax-polimer binder mix and a blend of fine (dm= 14 fim) and spherical gas atomised and coarse (dm= 23,3 um) and irregularly shaped water atomised 17-4 PH stainless steel powders in 0, 70, 80, 90 and 100 wt% ratios were prepared. By using classical MPIM processing cycle such as mixing, molding, solvent extraction and thermal debinding, sintering at 1250, 1280, 1300 and 13S0°C for 1 and 2 hours under hydrogen atmosphere, above mentioned feedstocks were homogenised at 1000°C for 1 hour under argon gas atmosphere. After iced- water quench, the same 17-4 PH stainless steel MPIM parts were aged artificially at 500 and 550°C for four hours under Ar-gas atmosphere. 17-4 PH stainless steel MPIM parts that were produced after all these above mentioned processing steps, were investigated in detail together with as- received powders, molded and debound samples, sintered, heat treated and aged samples by a combination of characterisation methods such as laser powder particulate size and size distribution analysis, optical and scanning electron metallography, SEM fractography and hardness measurements. At the and of this detailed investigation, not only the influence of the chemical composition of the powder blend of as-received powders in the prepared feedstock but also the different methods of debinding techniques, sintering time and temperature, homogenisation and ageing temperature on the microstructure-property relationships of 17-4 PH stainless steel MPIM parts were studied and determined. Science code : 3.022
Benzer Tezler
- Toz enjeksiyon kalıplama metoduyla üretilmiş 17-4PH paslanmaz çelik parçalara yapılan iki tip bor ilavesinin mikroyapı ve mekanik özelliklere etkisi
The Effect of two types of added boron on the microstructure and mechanical properties of 17-4PH stainless steel parts produced by powder injection molding
ÖZKAN GÜLSOY
Doktora
Türkçe
2003
Metalurji MühendisliğiMarmara ÜniversitesiMetal Eğitimi Ana Bilim Dalı
PROF. DR. SERDAR SALMAN
DOÇ. DR. SUNULLAH ÖZBEK
- Toz enjeksiyon kalıplama ile üretilmiş Ti-6Al-4V parçalarda işlem, yapı ve özellik ilişkileri
Relationships between processing, structure and properties at Ti-6Al-4V parts made by powder injection molding
YAŞAR ÇAKAR
Yüksek Lisans
Türkçe
2006
Metalurji MühendisliğiGazi ÜniversitesiMetal Eğitimi Ana Bilim Dalı
PROF. DR. SEDAT ÖZBİLEN
- Suda çözünebilir bağlayıcılı steatit besleme stokundan TEK ile üretilmiş ham parçalardan bağlayıcı alma işleminin araştırılması
Investigating of binder removal process from the compacts with water soluble binder component and steatit feedstock fabricated by PIM
ZİYA DOĞAN POLATKAN
Yüksek Lisans
Türkçe
2004
Teknik EğitimGazi ÜniversitesiMakine Eğitimi Ana Bilim Dalı
Y.DOÇ.DR. ÇETİN KARATAŞ
- Toz enjeksiyon kalıplama ile steatitten üretilmiş parçaların sinterleme davranışlarının araştırılması
Investigation of sintering behaviours of steatite parts produced by powder injection molding
MAHMUT BERBER
Yüksek Lisans
Türkçe
2005
Makine MühendisliğiGazi ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. İBRAHİM USLAN
- Toz enjeksiyon kalıplama yöntemi ile üretilmiş titanyumun yapay tükürük ortamında korozyon davranışının incelenmesi
An investigation of corrosion behaviour of powder injection moulded titanium in artificial saliva
RAMAZAN KURT
Yüksek Lisans
Türkçe
2008
Makine MühendisliğiKarabük ÜniversitesiMetal Eğitimi Ana Bilim Dalı
DOÇ. DR. ŞENNUR CANDAN