Bor karbür-alüminyum kompozitlerinin üretimi ve karakterizasyonu
Processing and characterization of boron carbide-aluminium composites
- Tez No: 109829
- Danışmanlar: DOÇ.DR. FERHAT KARA, DOÇ.DR. SERVET TURAN
- Tez Türü: Doktora
- Konular: Seramik Mühendisliği, Ceramic Engineering
- Anahtar Kelimeler: Sızdırma, Islatma, Zırh, Alüminyum, Bor karbür, Karakterizasyon, Kompozitler, İnfiltrasyon, Infiltration, Wetting, Armour 11, Aluminum, Boron carbide, Characterization, Composites
- Yıl: 2001
- Dil: Türkçe
- Üniversite: Anadolu Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Seramik Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET Doktora Tezi BOR KARBÜR-ALÜMİNYUM KOMPOZİTLERİNİN ÜRETİMİ VE KARAKTERİZASYONU GÜRSOYARSLAN Anadolu Üniversitesi Fen Bilimleri Enstitüsü Seramik Mühendisliği Anabilim Dalı Danışman: Doç. Dr. Ferhat KARA 2001 Bu tezde, üretim maliyeti düşük ve seri üretime uygun olan sızdırma yöntemi ile hafif, yoğun ve tok B4C-AI kompozitlerinin üretimi ve karakterizasyonu incelenmiştir. B4C-AI kompozitlerinin Ar atmosferi altında ve 985°-1370°C sıcaklık aralığında reaktif ıslatma ile üretilebileceği görülmüştür. Üretilen kompozitlerde oluşan fazlar ve miktarları kantitatif x-ışınları analizi ile sistematik olarak tespit edilmiştir. B4C ile Al arasındaki tepkime hızının sızdırma koşullarının, B4C tozlarının tane boyutunun ve yüzey kimyasının değiştirilerek kontrol edilebileceği görülmüştür. Bor karbürün alüminyum ile reaksiyonu sonucu, sırası ile, A13BC ve* A1B2 fazlan oluşmakta ve AI3BC fazı alüminyumun bor karbürü ıslatmasına yol açmaktadır. Üretilen kompozitlerin mekanik özellikleri süreç koşullarına bağlı olarak değişmekte ve kontrol edilebilmektedir. Kompozitlerin tokluğunun artan serbest alüminyum miktarı ve ligament boyutu ile arttığı görülmüştür. Yapılan balistik deneyler, üretilen B4C-AI kompozitlerinin çoklu çarpmalara dayanıklı zırh malzemesi olarak kullanım potansiyeline sahip olduğunu göstermektedir.
Özet (Çeviri)
ABSTRACT PhD Thesis PRODUCTION AND CHARACTERISATION OF BORON CARBIDE-ALUMINIUM COMPOSITES GÜRSOY ARSLAN Anadolu University Graduate School of Natural and Applied Sciences Ceramic Engineering Program Supervisor: Assoc. Prof. Dr. Ferhat KARA 2001 In this thesis, production and characterization of light, dense and tough B4C-A1 composites that have been produced by the cost effective melt infiltration technique are undertaken. It was observed that B4C-A1 composites could be produced by reactive infiltration at a temperature range between 985° and 1370 "C in an Ar atmosphere. The phases present and their quantities in the composites were determined systematically by quantitative x-ray analysis. It was found that by changing infiltration conditions, particle size and surface chemistry of B4C particles the reaction rate between B4C and Al could be controlled. As a result of a reaction between B4C and Al, A13BC and A1B2 are the mainly forming phases. It is the A13BC phase that leads to the wetting of B4C by aluminium. The mechanical properties of the produced composites are observed to vary depending on the processing conditions but the properties can be controlled. Fracture toughness of composites is observed to increase with the increasing content of free aluminium and the size of ligaments. Ballistic testing of the composites has shown that they have a potential to be used as armour materials with multi-hit performance.
Benzer Tezler
- Bor karbür esaslı seramik metal kompozitlerinin ultrases dalga hız metodu ile ortalama tanecik boyutlarının tayini
The mean grain size determination by ultrasonic velocity technique in basic boron carbide of ceramic metal composites
TUBA ÖZDEMİR
Yüksek Lisans
Türkçe
2005
Fizik ve Fizik MühendisliğiAfyon Kocatepe ÜniversitesiFizik Ana Bilim Dalı
YRD. DOÇ. DR. RIDVAN ÜNAL
- Bor karbür/alüminyum kompozitlerinin üretimi
The Production of boron carbioe/aluminium composites
ÖZGÜR ÖZDEMİR
- Synthesis of the BN-AIN composites by carbothermal reduction and nitridition of B4C-Al2O3 mixtures
AIN-BN kompozitlerinin reaksiyon sinterlenmesi yöntemiyle üretimi
CEM ÇELİKER
Yüksek Lisans
İngilizce
1997
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı (disiplinlerarası)
PROF. DR. ADNAN TEKİN
- Alüminyum matrisli B4C takviyeli kompozitlerin döküm yöntemi ile üretimi
Processing of B4C-reinforced al matrix by casting technique
FATİH TOPTAN
Yüksek Lisans
Türkçe
2006
Metalurji MühendisliğiYıldız Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. IŞIL KERTİ