Yüksek sıcaklıkta sinterlenmiş alümina (Al2O3) seramiklerin karakterizasyonu ve nötron radyasyonunun malzeme özelliklerine etkisinin araştırılması
Characterization of alumina ceramics sintered at high temperature and investigation of neutron radiation effect on the material properties
- Tez No: 106264
- Danışmanlar: DOÇ.DR. YASEMİN YARAR
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: Alümina, Seramik, Radyasyon, Karakterizasyon, Nötron, Alümina seramik, Sinterleme, Alumina, Ceramic, Radiation, Characterization, Neutron VI, Alumina ceramic, Neutron, Sintering
- Yıl: 2001
- Dil: Türkçe
- Üniversite: Yıldız Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET Bu çalışmada, İleri Teknoloji Seramiklerinden alümina seramiklerin karakterizasyonu yapılmış ve enerjitik nötron radyasyonunun malzeme özellikleri üzerine etkileri araştırılmıştır. Bu amaçla, değişik alumina tozlan incelenmiş ve tane boyutları, granülometrik ve sinterlenme özellikleri saptanmıştır. Bu deneyimlerin sonucu olarak, deneyler için en uygun olan alümina seçilmiştir. Değişik boyut ve geometrilerde bir çok pelet hazırlanmış ve 1600°C'da sinterienmiştir. Daha sonra bu örneklerin fiziksel ve mekanik özellikleri saptanmıştır. Ayrıca, mikroyapının gözlenebilmesi için bu örneklerin optik ve SEM. fotoğrafları alınmıştır. Karakterizasyonun tamamlanmasından sonra, alümina örnekler SAMES T-400 nötron jeneratörü ve Pu-Be (Howitzer) nötron kaynağı kullanılarak ışınlanmıştır. Mekanik testler tekrar edilerek değişik enerjili nötronların malzeme üzerindeki etkileri incelenmiştir. Deneysel çalışmaların son adımında iletken kontaklara sahip alümina örnekler hazırlanmış ve nötron radyasyonu süresince ve sonrasında elektriksel direnç ve iletkenliğin değişimi saptanmaya çalışılmıştır. Sonuç olarak bütün deneysel veriler çizelge, grafik ve fotoğraflar halinde sunulmuş ve sonuçlar tartışılmıştır.
Özet (Çeviri)
ABSTRACT In this work, characterization of Alumina Ceramics, which is sintered at high temperature, was done and the effects of energetic neutron radiation on the material properties were investigated. For this purpose, different kind of alumina powers was studied and their grain sizes, granulometric and sintering characteristics were determined. As a result of these experiences, the most suitable one was chosen for the experiments. A lot of pellets in different sizes and geometries were prepared and sintered at 1600°C. Then, their physical and mechanical characteristics were determined. Besides, some optical and SEM photographs of the samples were taken for the observation of microstructure. Having determined the characteristic properties, alumina samples were irradiated by utilizing the SAMES T-400 neutron generator and Pu-Be source (Howitzer). By performing the mechanical tests, the effect of neutrons of different energies on the material properties was examined. In the last step of the experimental studies, some alumina samples having conductive contacts were prepared and the changes of the electrical resistivity and conductivity during and after neutron irradiation were tried to determine. Consequently, experimental data were presented in tables, graphs and the photographs and the results were discussed.
Benzer Tezler
- Alümina esaslı seramiklerin sertlik deneyleri
Hardness testing of alumina based ceramics
ERDOĞAN AYDIN ÖZER
- Farklı sinterleme ve sıcaklıklarının %2 MnO ve %2 TiO2 katkılı alümina seramiğinin mikroyapısal ve fiziksel özelliklerine olan etkileri
Effects of different sintering temperatures on the microstructural and physical properties of an alumina veramic doped with 2 Wt.% MnO and 2 Wt.%
UTKU İNAN
Yüksek Lisans
Türkçe
2005
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF.DR. LÜTFİ ÖVEÇOĞLU
- Alümina içeren seramik kompozitlerin fiziksel özelliklerinin incelenmesi
Die Untersuchung der physikalischan eigenschaften von A12O3-gehaltigen keramischen komposite-werkstoffen
SUAT YILMAZ
- Alkilaromatik karışımların hidrodealkilasyonu-hidrokrakingi; katalizör geliştirilmesi
Hydrodealkylation-hydrocracking of alkylaromatic mixture; catalyst development
AYTEN ATEŞ
Doktora
Türkçe
2003
Kimya MühendisliğiAnkara ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. HASİP YENİOVA
- Test of biomaterials in biological systems
Biyomalzemelerin biyolojik sistemlerde test edilmesi
MERT SUDAĞIDAN
Yüksek Lisans
İngilizce
2001
Biyoteknolojiİzmir Yüksek Teknoloji EnstitüsüBiyoteknoloji Ana Bilim Dalı
DOÇ.DR. HATİCE GÜNEŞ