Üç farklı kalsiyum silikat içerikli materyalin farklı irrigasyon solüsyonlarında dentine bağlanma dayanımlarının değerlendirilmesi
Evaluation of the dentin bond strength of three different calcium silicate-containing materials in different irrigation solutions
- Tez No: 1017582
- Danışmanlar: PROF. DR. İHSAN FURKAN ERTUĞRUL
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: bağlanma dayanımı, irrigasyon solüsyonu, kök kanal patı, bond strength, irrigation solution, root canal sealer
- Yıl: 2026
- Dil: Türkçe
- Üniversite: Pamukkale Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Endodonti Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu in vitro çalışmanın amacı, üç farklı kalsiyum silikat içerikli materyalin (Bio-C Sealer (Angelus), Bio-Root Flow (Septodont) ve Dia-Root Bio Sealer (DiaDent)) farklı irrigasyon solüsyonlarında (NaOCl, EDTA, Distile Su) gösterdiği bağlanma dayanımlarını değerlendirmektir. Yöntem: Bu in vitro çalışmada tek köklü mandibular premolar dişler kullanılmıştır. Kök kanalları, glide patholuşturulmasının ardından resiprokal hareketle çalışan T-Endo Must R25 ve R40 nikel-titanyum eğe sistemi (Dentac, İstanbul, Türkiye) kullanılarak final apikal çap No:40 olacak şekilde prepare edilmiştir. Preparasyon sırasında her eğe değişiminden sonra 2 mL %5,25 sodyum hipoklorit (NaOCl) uygulanmıştır. Örnekler, uygulanan final irrigasyon protokolleri ve kök kanal patlarına göre gruplara ayrılmıştır. Final irrigasyon işlemlerinde 5 mL %5,25 NaOCl, 5 mL %17 EDTA ve 5 mL distile su kullanılmış; irrigasyon solüsyonları EndoActivator cihazı ile 1 dakika süreyle sonik olarak aktive edilmiştir. Sonik aktivasyon uygulanan örnekler lateral kompaksiyon yöntemi kullanılarak üç farklı kalsiyum silikat içerikli kök kanal patı ile doldurulmuştur. Tüm örnekler 37°C'de %100 nemli ortamda 1 hafta süreyle bekletilmiştir. Ardından örneklerden kök apeksinden itibaren 4 mm ve 9 mm seviyelerinde 2 mm kalınlığında kesitler elde edilmiş ve push-out bağlanma dayanımı testi uygulanmıştır. Kopma kuvvetleri bağlanma alanına oranlanarak megapaskal (MPa) cinsinden hesaplanmıştır. Elde edilen veriler istatistiksel olarak analiz edilmiş ve anlamlılık düzeyip<0,05 olarak kabul edilmiştir. Bulgular: NaOCl kullanılan gruplarda bağlanma dayanımı değerleri, EDTA ve distile su kullanılan gruplara kıyasla istatistiksel olarak anlamlı derecede daha yüksek bulunmuştur (p<0,05). Tüm gruplarda 4 mm seviyesinden elde edilen bağlanma dayanımı değerleri, 9 mm seviyesine göre istatistiksel olarak anlamlı derecede daha yüksek saptanmıştır (p<0,05). Kök kanal patları arasında genel bağlanma dayanımı açısından anlamlı bir fark saptanmamıştır (p> 0,05). Ancak alt grup analizlerinde, EDTA ile son irrigasyon yapılan gruplarda ve 9 mm seviyesinde distile su grubunda, patlar arasında istatistiksel olarak anlamlı farklılıklar belirlenmiştir (p< 0,05). Sonuç: Kalsiyum silikat içerikli kök kanal patlarının bağlanma dayanımları, kullanılan final irrigasyon solüsyonuna bağlı olarak değişmektedir. Smear tabakasının uzaklaştırılmasında yaygın olarak kullanılan EDTA'nın, kalsiyum silikat içerikli kök kanal patlarının bağlanma dayanımını olumsuz yönde etkilediği görülmüştür.
Özet (Çeviri)
Objective: The aim of this in vitro study was to evaluatethe push-out bond strength of three calciumsilicate–based root canal sealers—Bio-C Sealer (Angelus), Bio-Root Flow (Septodont), and Dia-Root Bio Sealer (DiaDent)—following the use of differentfinal irrigation solutions (NaOCl, EDTA, and distilledwater). Methods: In this in vitro study, single-rootedmandibular premolar teeth were used. Following glidepath preparation, the root canals were instrumented to a final apical size of #40 using the T-Endo Must R25 and R40 nickel-titanium file system (Dentac, Istanbul, Türkiye) operated in reciprocating motion. Duringinstrumentation, 2 mL of 5.25% sodium hypochlorite(NaOCl) was used after each file change. The specimenswere divided into groups according to the final irrigationprotocols and root canal sealers used. For the final irrigation procedures, 5 mL of 5.25% NaOCl, 5 mL of 17% EDTA, and 5 mL of distilled water were used, and the irrigating solutions were sonically activated for 1 minute using the EndoActivator device. The specimenssubjected to sonic activation were obturated using thelateral compaction technique with three differentcalcium silicate-based root canal sealers. All specimenswere stored at 37°C under 100% humidity for 1 week. Subsequently, 2-mm-thick sections were obtained fromthe specimens at 4 mm and 9 mm levels from the rootapex, and a push-out bond strength test was performed. The dislodgement forces were divided by the bondingarea and calculated in megapascals (MPa). The obtaineddata were statistically analyzed, and the level of significance was set at p < 0.05. Results: Bond strength values were significantly higherin the NaOCl groups compared with the EDTA and distilled water groups (p< 0.05). In all groups, bondstrength values obtained at the 4-mm level weresignificantly higher than those at the 9-mm level (p< 0.05). No statistically significant difference in overallbond strength was observed among the root canal sealers(p> 0.05). However, subgroup analyses revealedstatistically significant differences among the sealers in the EDTA groups and in the distilled water group at the9-mm level (p< 0.05). Conclusion: The bond strength of calciumsilicate–based root canal sealers varies depending on thefinal irrigation solution used. EDTA, which is widelyemployed for smear layer removal in endodontics, wasfound to adversely affect the bond strength of calciumsilicate–based root canal sealers.
Benzer Tezler
- Açık apeksli dişlerde farklı apikal tıkaç teknikleriyle yerleştirilen kalsiyum silikat içerikli materyallerinmarjinal adaptasyonları ve apikal ekstrüzyonlarının mikro-BT iledeğerlendirilmesi
Evaluation of marginal adaptation and apical extrusion of calcium silicate-containing materials using different apical obturation techniques in teeth with open apices, assessed by micro-CT
ECEM ÖZGÜR
Diş Hekimliği Uzmanlık
Türkçe
2026
Diş HekimliğiAnkara ÜniversitesiEndodonti Ana Bilim Dalı
PROF. DR. BERKAN ÇELİKTEN
- Derı̇n çürüklü süt dı̇şlerı̇nı̇n pulpa kuafajında farklı kapaklama ajanlarının etkı̇nlı̇ğı̇nı̇n in-vivo olarak değerlendı̇rı̇lmesı̇
Effectiveness of the different pulp capping material in pulp capping therapy of primary teeth with deep dentin caries: in vivo evaluation
NACİYE NUR ŞAHİN
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş Hekimliğiİzmir Katip Çelebi ÜniversitesiPedodonti Ana Bilim Dalı
DOÇ. DR. MERVE AKÇAY
- Farklı yapıdaki kalsiyum silikat simanların kompozit ve kompomer restoratif materyallere olan bağlantısının değerlendirilmesi
Başlık çevirisi yok
FATIMA KÜBRA ALTINAY KARACA
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiSivas Cumhuriyet ÜniversitesiÇocuk Diş Hekimliği Ana Bilim Dalı
PROF. DR. FATİH ÖZNURHAN
- Eğimli kök kanallarında farklı kök kanal patlarıyla yapılan kanal dolgusundaki boşlukların MİKRO-BT ile incelenmesi
MİCRO-CT evaluation of voids in root canal filling with different root canal sealers in curved root canals
İLÇİ BERK İÇMEZ
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiAnkara ÜniversitesiEndodonti Ana Bilim Dalı
PROF. DR. AYLİN KALAYCI
- Biyomedikal uygulamalar için kobalt/ bor eş katkılı 45S biyocamın sentezi ve karakterizasyonu
Synthesis and characterization of cobalt/boron co-added 45S biocam for biomedical applications
HATİCE GÜRDAL
Yüksek Lisans
Türkçe
2022
BiyomühendislikKarabük ÜniversitesiBiyomedikal Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ AMMAR ZEIDAN GHAILAN ALSHEMARY
DR. ÖĞR. ÜYESİ DAVER ALİ