Agregaya farkli tipte atik malzemeler ikame edilerek oluşturulan harçlarin duvar kesme performansina etkisinin araştirilmasi
Effect of mortars with construction and demolition waste as aggregate replacements on masonry shear performance
- Tez No: 1016963
- Danışmanlar: DR. ÖĞR. ÜYESİ ORHAN GAZİ ODACIOĞLU, DOÇ. DR. MELEK AKGÜL
- Tez Türü: Yüksek Lisans
- Konular: Deprem Mühendisliği, İnşaat Mühendisliği, Earthquake Engineering, Civil Engineering
- Anahtar Kelimeler: Örgü Harcı, İnşaat ve Yıkıntı Atığı, Beton Atığı, Seramik Atığı, Cam Atığı, Triplet Deneyi, Kesme Dayanımı, Yığma Yapı, Beton, Cam tozları, Seramik tozları, İnşaat malzemeleri, İnşaat mühendisliği, İnşaat projeleri, İnşaat sektörü, İnşaat teknolojisi, Masonry Mortar, Construction and Demolition Waste, Concrete Waste, Ceramic Waste, Glass Waste, Triplet Test, Shear Strength, Masonry Structure, Concrete, Glass powders, Ceramic powders, Civil engineering, Construction projects, Construction sector, Construction technology
- Yıl: 2026
- Dil: Türkçe
- Üniversite: Kırıkkale Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
- Bilim Dalı: İnşaat ve Yapı Mühendisliği Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Deprem riski, yığma yapıların güvenliği ile inşaat ve yıkıntı atıklarının sürdürülebilir geri kazanımı sorunlarını ortak bir mühendislik ekseninde ele almaktadır. Bu bağlamda, örgü harcı agregasına ikame edilen atık agregaların, tuğla-harç ara yüzey kesme davranışına etkisinin incelenmesi ve çevresel fayda ile yapısal performans birlikte değerlendirilmesine ihtiyaç duyulmuştur. Bu çalışmada, yığma yapılarda kullanılan örgü harçlarında doğal dere kumu yerine farklı türlerde inşaat ve yıkıntı atıklarının kullanılabilirliği araştırılmıştır. Bu amaçla beton atığı, seramik atığı ve cam atığı agregaları, doğal agregaya hacimce %5, %10 ve %15 oranlarında ikame edilerek farklı örgü harcı serileri üretilmiştir. Üretilen harç numuneleri 3, 28 ve 90 günlük kür süreleri sonunda fiziksel, mekanik ve mikro yapısal özellikler bakımından incelenmiştir. Bu kapsamda etüv kurusu birim hacim ağırlık, porozite, kütlece su emme, eğilme dayanımı ve basınç dayanımı deneyleri gerçekleştirilmiş; ayrıca 28 günlük numuneler üzerinde SEM analizleri yapılmıştır. Bunun yanında, atık agrega ikameli örgü harçlarının tuğla-harç ara yüzey kesme performansını belirlemek amacıyla triplet deneyleri uygulanmıştır. Deney sonuçlarına göre, atık agrega kullanımı genel olarak harçların porozite ve su emme değerlerini artırmış, etüv kurusu birim hacim ağırlıklarını ise azaltmıştır. Kür süresinin artmasıyla birlikte tüm serilerde porozite ve su emme oranlarında azalma, mekanik dayanımlarda ise artış gözlenmiştir. Beton atığı içeren serilerde özellikle %10 ve %15 ikame oranlarında basınç dayanımı ve kesme performansı bakımından olumlu sonuçlar elde edilmiştir. Seramik atığı içeren harçlarda %10 ikame oranı, mikro yapı ve mekanik dayanım açısından en dengeli sonuçları vermiştir. Cam atığı içeren serilerde ise düşük ikame oranlarında kabul edilebilir performans elde edilmesine rağmen, %10 ve %15 ikame oranlarında özellikle ara yüzey aderansı ve kalıcı kesme dayanımı bakımından azalma meydana gelmiştir. Triplet deneyleri sonucunda, normal gerilmenin artmasıyla tüm serilerde maksimum ve kalıcı kesme dayanımlarının arttığı belirlenmiştir. Genel olarak beton ve seramik atığı ikameli harçların, cam atığı ikameli harçlara göre tuğla-harç ara yüzey kesme performansı bakımından daha başarılı olduğu görülmüştür. Sonuç olarak, beton, seramik ve cam atıklarının uygun oranlarda örgü harcı üretiminde doğal agregaya ikame olarak kullanılabileceği; bu kullanımın hem sürdürülebilir yapı malzemesi üretimine katkı sağlayabileceği hem de yığma yapı harçlarının mühendislik özelliklerini iyileştirebileceği belirlenmiştir.
Özet (Çeviri)
Seismic risk, the safety of masonry structures, and the sustainable recovery of construction and demolition wastes are addressed within a common engineering framework. In this context, it has become necessary to investigate the effect of waste aggregates substituted for masonry mortar aggregate on the brick–mortar interface shear behavior, and to evaluate environmental benefits together with structural performance. In this study, the usability of different types of construction and demolition wastes as partial replacements for natural river sand in masonry mortars was investigated. For this purpose, concrete waste, ceramic waste and glass waste aggregates were used as partial replacements for natural aggregate at volumetric ratios of 5%, 10% and 15%. The produced mortar specimens were examined in terms of physical, mechanical and microstructural properties after 3, 28 and 90 days of curing. Within this scope, oven-dry unit weight, porosity, water absorption, flexural strength and compressive strength tests were carried out. In addition, SEM analyses were performed on 28-day mortar specimens. Furthermore, triplet tests were conducted to determine the effect of waste aggregate-substituted mortars on the shear performance of the brick-mortar interface. According to the experimental results, the use of waste aggregates generally increased the porosity and water absorption values of the mortars, while decreasing their oven-dry unit weight. With increasing curing time, porosity and water absorption values decreased, whereas mechanical strength values increased in all series. In the concrete waste aggregate series, especially 10% and 15% replacement ratios provided favorable results in terms of compressive strength and shear performance. In the ceramic waste aggregate series, the 10% replacement ratio exhibited the most balanced performance in terms of microstructure and mechanical strength. In the glass waste aggregate series, acceptable performance was obtained at low replacement ratios; however, at 10% and 15% replacement ratios, reductions were observed particularly in interface adhesion and residual shear strength. The triplet test results showed that both maximum and residual shear strengths increased with increasing normal stress in all series. In general, mortars containing concrete and ceramic waste aggregates exhibited better brick-mortar interface shear performance than those containing glass waste aggregates. As a result, it was determined that concrete, ceramic and glass wastes can be used as partial replacements for natural aggregate in masonry mortar production at suitable ratios. This approach may contribute to sustainable construction material production while also improving the engineering properties of masonry mortars.
Benzer Tezler
- Değişken geometride ve doğrultuda yapay agregaya sahip yüksek dayanımlı betonların çarpma etkisi altında davranışının incelenmesi
Investigation of fracture mechanism and behaviour of high performance concretes within artificial aggregates in variable dimensions and directions under impact loading
VOLKAN ERKAN
Yüksek Lisans
Türkçe
2017
İnşaat MühendisliğiGazi Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. ABDUSSAMET ARSLAN
- Kendiliğinden yerleşen taze betonda değiştirilmiş L- kutusu yöntemiyle segregasyon kontrolü
Segregation controlling of fresh self compacting concrete by modified L- box
HASAN BAKIRCI
Yüksek Lisans
Türkçe
2011
İnşaat MühendisliğiHarran Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. KAZIM TÜRK
YRD. DOÇ. DR. PAKİ TURĞUT
- Prediction of early-age mechanical properties of high strength concrete with pozzolans by using statistical methods
İstatistik yöntemler kullanılarak puzolan katkılı yüksek dayanmlı betonların erken yaş mekanik özelliklerinin tahmini
MUZAFFER UMUR DALGIÇ
Yüksek Lisans
İngilizce
2022
İnşaat Mühendisliğiİstanbul Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. YILMAZ AKKAYA
- Tekne konstrüksiyonunda kullanılabilecek ferrosement yapının mekanik davranışı ve en uygun malzeme bileşenlerinin belirlenmesi
Die Bestimmung der optimalen materialzusammensetzung und das mechanische verhalten des fur den bootsbau geeigneten ferrocements
HALUK KAYA
- Oksidan stresle giden patolojilerde antioksidan savunma sistemleri ve trobosit fonksiyonları ilişkisi
The Interactions between antioxidative defence system and platelet functions in the patients with oxidative stress related diseases
DEMET TEKİN