Üç boyutlu yazıcılar ile üretilen rezin materyallerinin mekanik ve optik özelliklerinin değerlendirilmesi
Evaluation of the mechanical and optical properties of resin materials produced using 3D printers
- Tez No: 1015020
- Danışmanlar: DOÇ. DR. CENNET ELÇİN SAĞIRKAYA
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: 3B baskı, dental reçine, renk stabilitesi, iki eksenli eğme dayanımı, termal yaşlandırma, 3D printing, dental resin, color stability, biaxial flexural strength, thermal aging
- Yıl: 2026
- Dil: Türkçe
- Üniversite: Ordu Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu tez çalışmasında, üç boyutlu (3B) yazıcılar ile farklı kalınlıklarda üretilen iki daimî restorasyon materyalinin, termal yaşlandırma öncesi ve sonrası optik ve mekanik özelliklerinin değerlendirilmesi amaçlanmıştır. Materyal Metot: Bu çalışmada, eklemeli üretim yöntemiyle elde edilen iki farklı 3B baskı reçine materyalinin (Print Crowntec ve VarseoSmile TriniQ) her biri için 90 adet olmak üzere toplam 180 adet disk formunda örnek 1 mm, 1,5 mm ve 2 mm kalınlıklara sahip olacak şekilde hazırlanmıştır (n=30). Her bir kalınlık grubundaki örnekler rastgele iki alt gruba ayrılarak; bir alt gruba herhangi bir işlem yapılmamış, diğer alt grup başlangıç renk ölçümünün ardından termal döngü işlemine maruz bırakılmıştır. Termal yaşlandırma işlemi yapılan gruptaki örneklerden işlem öncesinde ve sonrasında renk ölçümleri gerçekleştirilmiş ve renk değişimi değerleri CIEDE2000 (ΔE₀₀) formülü kullanılarak hesaplanmıştır. Daha sonra her iki gruptaki örneklerin iki eksenli eğme dayanımı değerleri, üç top üzeri piston (piston-on-three-ball) yöntemi kullanılarak belirlenmiştir. Veriler SPSS 26.0 programında analiz edilmiş; normallik ve varyans homojenliği varsayımları sırasıyla Shapiro–Wilk ve Levene testleri ile değerlendirilmiştir. Renk değişimi verileri için iki yönlü varyans analizi, eğme dayanımı verileri için ise üç yönlü varyans analizi (ANOVA) uygulanmış (α=,05), anlamlı farklılık saptanan durumlarda Tukey HSD post-hoc testi kullanılmıştır. Bulgular: Termal yaşlandırma sonrasında her iki materyalde de renk değişim değerlerindeki artış istatistiksel olarak anlamlı bulunmamış ve tüm gruplarda ΔE₀₀ değerlerinin klinik kabul edilebilir sınırın (1,8) altında kaldığı belirlenmiştir. ΔE₀₀ değerleri VarseoSmile TriniQ grubunda 0,78–0,86, Crowntec grubunda ise 0,74–0,79 aralığında bulunmuş; kalınlık artışı ile renk değişimi değerlerinde azalma eğilimi izlenmiştir. Mekanik değerlendirmelerde Crowntec materyali çoğu grupta VarseoSmile TriniQ materyaline göre daha yüksek eğme dayanımı göstermiştir. En yüksek dayanım değeri Crowntec 1 mm termal yaşlandırma uygulanmayan grubunda 131,72 ± 4,07 MPa, en düşük dayanım değeri ise VarseoSmile TriniQ 2 mm termal yaşlandırma uygulanan grubunda 100,98 ± 2,15 Mpa olarak elde edilmiştir. Genel olarak kalınlık artışı ve termal yaşlandırmanın her iki materyalde de eğme dayanım değerlerini düşürdüğü saptanmıştır. Sonuç: Bu tez çalışmasında değerlendirilen VarseoSmile TriniQ ve Crowntec üç boyutlu baskı daimî restorasyon materyallerinin her ikisinin de klinik açıdan kabul edilebilir renk stabilitesi ve yeterli mekanik performans sergilediği belirlenmiştir. Termal yaşlandırma sonrası tüm gruplarda renk değişimi değerleri klinik kabul edilebilir sınırlar içerisinde kalırken, iki eksenli eğme dayanımının reçine türü, örnek kalınlığı ve yaşlandırma koşullarından anlamlı düzeyde etkilendiği saptanmıştır. Crowntec materyali çoğu grupta daha yüksek dayanım değerleri göstermiş, kalınlık artışı ve termal yaşlandırmanın ise her iki materyalde de dayanımı azaltıcı etki oluşturduğu görülmüştür. Bu bulgular doğrultusunda, klinik uygulamalarda materyal seçimi ve restorasyon kalınlığı planlanırken estetik ve mekanik gereksinimlerin birlikte değerlendirilmesi gerekmektedir.
Özet (Çeviri)
Aim: The aim of this thesis was to evaluate the optical and mechanical properties of two permanent restorative materials fabricated using three-dimensional (3D) printing at different thicknesses, before and after thermal aging. Materials and Methods: In this study, a total of 180 disc-shaped specimens were prepared from two different 3D-printed resin materials (Print Crowntec and VarseoSmile TriniQ), with 90 specimens for each material. The specimens were fabricated in three different thicknesses (1.0 mm, 1.5 mm, and 2.0 mm) (n=30). Each thickness group was randomly divided into two subgroups: one subgroup received no treatment, while the other subgroup underwent thermal cycling after baseline color measurements. For the thermally aged group, color measurements were performed before and after the aging process, and color differences were calculated using the CIEDE2000 (ΔE₀₀) formula. Subsequently, the biaxial flexural strength of all specimens was determined using the piston-on-three-ball test method. Statistical analyses were performed using SPSS 26.0 software. Normality and homogeneity of variance were assessed using the Shapiro–Wilk and Levene tests, respectively. Two-way ANOVA was applied for color change data, and three-way ANOVA was used for flexural strength data (α = 0.05). Tukey HSD post-hoc test was performed when significant differences were detected. Results: After thermal aging, the increase in color change values for both materials was not statistically significant, and all ΔE₀₀ values remained below the clinically acceptable threshold (1.8). The ΔE₀₀ values ranged between 0.78–0.86 for VarseoSmile TriniQ and 0.74–0.79 for Crowntec, with a decreasing trend observed as thickness increased. In mechanical evaluations, Crowntec demonstrated higher flexural strength values than VarseoSmile TriniQ in most groups. The highest strength value was obtained in the Crowntec 1.0 mm non-aged group (131.72 ± 4.07 MPa), while the lowest value was observed in the VarseoSmile TriniQ 2.0 mm aged group (100.98 ± 2.15 MPa). Overall, both increased thickness and thermal aging led to a reduction in flexural strength for both materials. Conclusion: Both VarseoSmile TriniQ and Crowntec 3D-printed permanent restorative materials demonstrated clinically acceptable color stability and adequate mechanical performance. While color changes remained within clinically acceptable limits after thermal aging, biaxial flexural strength was significantly affected by resin type, specimen thickness, and aging conditions. Crowntec generally exhibited higher strength values, whereas increased thickness and thermal aging had a decreasing effect on strength in both materials. These findings suggest that both aesthetic and mechanical requirements should be considered when selecting materials and planning restoration thickness in clinical practice.
Benzer Tezler
- Konvansiyonel yöntemle ve 3 boyutlu yazıcıyla üretilen rezin dişlerin mekanik ve optik özelliklerinin karşılaştırılması
Comparison of the mechanical and optical properties of resin teeth produced by conventional methods and 3D printing
SEMİH BOZDOĞAN
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiUşak ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. MEHMET ALİ GÜNGÖR
- Üç farklı teknikle üretilen posterior adeziv restorasyonların mekanik özelliklerinin İn-vitro incelenmesi
In-vitro evaluation of the mechanical properties of posterior adhesive restorations fabricated using three different techniques
GÖZDE ACAR
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiEge ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. CEM PEŞKERSOY
- 3 boyutlu yazıcılar ile üretilen oklüzal splint materyallerinin mekanik ve yüzey özelliklerine yaşlandırmanın etkisinin in-vitro değerlendirilmesi
In-vitro evaluation of the effect of aging on the mechanical and surface properties of occlusal splint materials produced with 3d printers
MERT HAMİT BIKMAZ
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiAnkara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. SEMA MURAT
- 3 boyutlu yazıcılar ve geleneksel yöntemlerle kullanılan geçici kron materyallerinin kırılma dayanımlarının değerlendirilimesi
Başlık çevirisi yok
AYTAN SHAHMALIYEVA
Diş Hekimliği Uzmanlık
Türkçe
2026
Diş HekimliğiAkdeniz ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ULVİYE ŞEBNEM BÜYÜKKAPLAN
- Farklı CAD/CAM protez kaide materyallerinin mekanik özelliklerinin incelenmesi
Investigation of mechanical properties of different CAD/CAM denture base materials
SEÇİL SAKARYA
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiAtatürk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. FUNDA BAYINDIR